Ni-Fe/γ-Al2O3双金属催化剂的制备及其CO甲烷化性能研究

王　宁,  孙自瑾,  王永钊,  高晓庆,  赵永祥

downloadPDF
文章导航 > 燃料化学学报（中英文）  > 2011 >  39(03): 219-223
王　宁, 孙自瑾, 王永钊, 高晓庆, 赵永祥. Ni-Fe/γ-Al2O3双金属催化剂的制备及其CO甲烷化性能研究[J]. 燃料化学学报（中英文）, 2011, 39(03): 219-223.
引用本文: 王　宁, 孙自瑾, 王永钊, 高晓庆, 赵永祥. Ni-Fe/γ-Al2O3双金属催化剂的制备及其CO甲烷化性能研究[J]. 燃料化学学报（中英文）, 2011, 39(03): 219-223.
shu
WANG 　Ning, Sun-Zi-Jin, Wang-Yong-Zhao, Gao-Xiao-Qiang, Zhao-Yong-Xiang. Preparation of bimetallic Ni-Fe/γ-Al2O3 catalyst and its activity for CO methanation[J]. Journal of Fuel Chemistry and Technology, 2011, 39(03): 219-223.
Citation: WANG 　Ning, Sun-Zi-Jin, Wang-Yong-Zhao, Gao-Xiao-Qiang, Zhao-Yong-Xiang. Preparation of bimetallic Ni-Fe/γ-Al2O3 catalyst and its activity for CO methanation[J]. Journal of Fuel Chemistry and Technology, 2011, 39(03): 219-223.
shu

Ni-Fe/γ-Al2O3双金属催化剂的制备及其CO甲烷化性能研究

  • 1.山西大学化学化工学院| 精细化学品教育部工程研究中心| 山西 太原 030006|2.山西三维集团股份有限公司| 山西 洪洞 041603

基金项目: 山西省科技创新计划项目（2007101008）
详细信息
    通讯作者:

    赵永祥， Tel： 0351-7011587， Fax： 0351-7011688， E-mail： yxzhao@sxu.edu.cn

  • 中图分类号: O643.38

Preparation of bimetallic Ni-Fe/γ-Al2O3 catalyst and its activity for CO methanation

  • School of Chemistry and Chemical Engineering, Engineering Research Center for Fine Chemicals of Ministry of Education, Shanxi University, Taiyuan 030006, China|

    摘要
  • 摘要: 采用等体积浸渍法制备了Ni-Fe/γ-Al2O3双金属催化剂和Ni/γ-Al2O3、Fe/γ-Al2O3单金属催化剂，在连续流动微反装置上考察了催化剂的CO甲烷化催化活性，采用XRD、N2物理吸附、H2-TPR、H2-TPD和TPSR等手段对催化剂进行表征。结果表明，Ni-Fe/γ-Al2O3双金属催化剂中Ni、Fe之间产生了明显的相互作用，还原后催化剂中形成Ni-Fe合金，对氢气吸附量显著增加。在CO体积分数为0.5%、空速5000h-1、常压的反应条件下，Ni-Fe/γ-Al2O3双金属催化剂表现出高的甲烷化活性，220℃时将CO完全转化为甲烷。
    Abstract: Bimetallic Ni-Fe/γ-Al2O3 catalyst and monometallic Ni/γ-Al2O3, Fe/γ-Al2O3 catalysts were prepared by wet impregnation method; they were characterized by XRD, N2 physisorption, H2-TPR, H2-TPD and TPSR. The activity of these catalysts in CO methanation was investigated in a fixed-bed continuous flow reactor. A significant Ni-Fe interaction is observed in the bimetallic Ni-Fe/γ-Al2O3 catalyst; Ni-Fe alloy is formed during reduction, which can promote the adsorption of hydrogen. Under the reaction conditions of 0.5% CO, GHSV of 5000h-1 and atmosphere pressure, the bimetallic Ni-Fe/γ-Al2O3 catalyst exhibits high catalytic activity; CO can be completely converted into methane at 220℃.
    • HTML全文
    • 参考文献(0)
    • 相关文章
    • 施引文献
  • 资源附件(0)
  • 加载中
WeChat 点击查看大图
计量
  • 文章访问数:  1668
  • HTML全文浏览量:  17
  • PDF下载量:  817
  • 被引次数: 0
出版历程
  • 收稿日期:  2010-05-08
  • 修回日期:  2010-08-17
  • 刊出日期:  2011-03-31

目录

    /

    返回文章
    返回
    友情链接： 新型炭材料 中国科学院 中国知网 万方论文查重系统

    主办单位：中国科学院山西煤炭化学研究所 中国化学会主编：房倚天

    电子邮件：rlhx@sxicc.ac.cn

    版权所有 © 《燃料化学学报（中英文）》编辑部 本系统由 北京仁和汇智信息技术有限公司 开发    百度统计

    x 关闭 永久关闭

    2023年《燃料化学学报（中英文）》评优结果公布！