还原条件对NiFe2O4－δ结构稳定性及其催化分解CO2活性的影响

Nickel ferrite, NiFe2O4, with spinel structure was prepared by citrate coordination method. The samples were characterized by X-ray diffraction (XRD) thermal gravimetric analysis (TGA). When the weight of NiFe2O4 sample was 0.5g, the optimum reduction condition for the preparation of oxygendeficient nickel ferrite, NiFe2O4－δ, reduced by H2 was as follows: reduction temperature was 320℃, H2 flow rate was 40mL/min and reduction time was 3h. The results also showed that the higher reduction temperature and higher H2 flow rate as well as longer reduction time led to an excessive reduction of NiFe2O4－δ and the destructiveness of its spinel structure, resulting in the formation of FeNi alloy Fe(Ni) as well as α-Fe phase.