铁基助熔剂对皖北刘桥二矿煤的灰熔融特性影响研究

李继炳,  沈本贤,  李寒旭,  赵基钢,  王基铭

downloadPDF
文章导航 > 燃料化学学报（中英文）  > 2009 >  37(03): 262-265
李继炳, 沈本贤, 李寒旭, 赵基钢, 王基铭. 铁基助熔剂对皖北刘桥二矿煤的灰熔融特性影响研究[J]. 燃料化学学报（中英文）, 2009, 37(03): 262-265.
引用本文: 李继炳, 沈本贤, 李寒旭, 赵基钢, 王基铭. 铁基助熔剂对皖北刘桥二矿煤的灰熔融特性影响研究[J]. 燃料化学学报（中英文）, 2009, 37(03): 262-265.
shu
LI Ji-Bing, Chen-Ben-Xian, Li-Han-Xu, Diao-Ji-Gang, Wang-Ji-Ming. Effect of ferrumbased flux on the melting characteristics of coal ash from coal blends using the Liuqiao No.2 coal mine in Wan-bei[J]. Journal of Fuel Chemistry and Technology, 2009, 37(03): 262-265.
Citation: LI Ji-Bing, Chen-Ben-Xian, Li-Han-Xu, Diao-Ji-Gang, Wang-Ji-Ming. Effect of ferrumbased flux on the melting characteristics of coal ash from coal blends using the Liuqiao No.2 coal mine in Wan-bei[J]. Journal of Fuel Chemistry and Technology, 2009, 37(03): 262-265.
shu

铁基助熔剂对皖北刘桥二矿煤的灰熔融特性影响研究

  • 1.

    华东理工大学 化学工程联合国家重点实验室, 上海 200237;

  • 2.

    中国石油化工股份有限公司安庆分公司| 安徽 安庆 246001; 3.安徽理工大学 化学工程学院, |安徽 淮南 232001

详细信息
    作者简介:

    李继炳（1964-）| 男| 安徽无为人| 博士研究生| 教授级高级工程师| 主要研究方向为煤气化工程。

    通讯作者:

    沈本贤， Tel: 021-64252851, Fax: 021-64252851。

  • 中图分类号: TQ038

Effect of ferrumbased flux on the melting characteristics of coal ash from coal blends using the Liuqiao No.2 coal mine in Wan-bei

  • 1.

    State Key Laboratory of Chemical Engineering, East China University of Science and Technology, Shanghai 200237, China|

  • 2.

    Anqing Branch Co.| SINOPEC| Anqing 246001| China;

    摘要
  • 摘要: 研究了铁基助熔剂对皖北刘桥二矿煤（AQ）灰熔融特征的影响，并对AQ煤灰在添加铁基助熔剂前后不同热处理温度下的矿物组成进行了XRD和红外光谱分析。结果表明,导致AQ煤灰熔点高的主要原因是1000℃以上形成的莫来石引起的；加入铁基助熔剂可以降低AQ煤灰的熔融温度；在高温下铁基助熔剂与煤灰中其他铝硅酸盐矿物发生反应，生成铁橄榄石和铁尖晶石等低温共熔化合物，从而使煤灰熔点明显下降。
    Abstract: The effect of ferrum-based flux on the melting characteristics of coal ash in coal blends from the Liu-qiao No.2 coal mine in Wan-bei (AQ) was investigated. The change of the compositions of mineral under various temperatures before and after adding ferrum-based flux into AQ was studied by XRD and FT-IR. Results show that the presence of mullite formed over 1000℃ increases the melting point of coal-ash, leading to high melting temperature of AQ coal-ash. The coal ash fusion temperature will be decreased by adding ferrum-based flux. The eutectic mixtures such as fayalite and hercynite are easily formed between ferrum compounds under high temperature, which remarkably decreases the coal ash fusion temperature.
    • HTML全文
    • 参考文献(0)
    • 相关文章
    • 施引文献
  • 资源附件(0)
  • 加载中
WeChat 点击查看大图
计量
  • 文章访问数:  1622
  • HTML全文浏览量:  31
  • PDF下载量:  897
  • 被引次数: 0
出版历程
  • 收稿日期:  2008-11-11
  • 修回日期:  2009-02-26
  • 刊出日期:  2009-06-30

目录

    /

    返回文章
    返回
    友情链接： 新型炭材料 中国科学院 中国知网 万方论文查重系统

    主办单位：中国科学院山西煤炭化学研究所 中国化学会主编：房倚天

    电子邮件：rlhx@sxicc.ac.cn

    版权所有 © 《燃料化学学报（中英文）》编辑部 本系统由 北京仁和汇智信息技术有限公司 开发    百度统计

    x 关闭 永久关闭

    2023年《燃料化学学报（中英文）》评优结果公布！