Effect of preparation condition on catalytic performance of Ni/ZrO2-SiO2 for methanation of coal gas
-
摘要: 采用浸渍法制备了ZrO2-SiO2复合载体和Ni质量分数为6%的Ni/ZrO2-SiO2催化剂,考察了载体制备时浸渍溶液pH值、焙烧温度和催化剂制备时的焙烧温度对Ni/ZrO2-SiO2催化剂煤气甲烷化反应性能的影响。采用X射线衍射、程序升温还原和扫描电子显微镜等方法对催化剂进行了表征。结果表明,载体浸渍溶液pH值为8.0~9.0, 载体焙烧温度为550 ℃,催化剂焙烧温度为450 ℃时,Ni/ZrO2-SiO2催化剂在煤气甲烷化反应中显示了最优的催化性能,CO转化率100%,CO2转化率1.8%,CH4生成速率16.6 mmol/(h·g)。进一步表征发现,制备ZrO2-SiO2复合载体时,增大浸渍溶液的pH值有利于形成粒径较小的亚稳态四方晶相ZrO2,可见四方晶相ZrO2更有利于甲烷化反应;载体焙烧温度会影响到NiO粒径的大小和其在催化剂表面的分散,温度过高和过低都会导致NiO粒径大小的不适宜以及分散性的降低;催化剂焙烧温度过高则会导致NiO与载体间的相互作用减弱,NiO分散性降低。Abstract: Ni/ZrO2-SiO2 catalysts with 6% Ni loading amount were prepared by impregnation. The ZrO2-SiO2 support was also synthesized by impregnation. Effects of pH value of the impregnating solution and calcination temperature of support and catalyst on activities of Ni/ZrO2-SiO2 catalysts were investigated. The catalysts were characterized using XRD,TPR and SEM measurements. Ni/ZrO2-SiO2(S5) catalyst exhibited excellent catalytic activity with 100% of CO conversion, 1.8% of CO2 conversion and 16.6 (mmol·h-1·g-1) of CH4 formation rate. The preparation conditions were as follows:pH value of the impregnating solution, 8.0~9.0, calcination temperature of support and catalyst, 550 ℃ and 450 ℃.The mathanation activity of Ni/ZrO2-SiO2 was strongly influenced by the ZrO2 phase change. The catalyst with tetragonal zirconia showed higher catalytic activity. The increase of pH value of the impregnating solution was in favor of forming small tetragonal zirconia. The calcination temperature of support influenced the grain size and the dispersity of NiO, unsuitable temperature might lead to ill-fitted grain size and aggregation. Exorbitant calcination temperature could weaken interaction between NiO and the support, and lowered the dispersity of NiO.
-
Key words:
- nickel /
- ZrO2-SiO2 /
- carbon monoxide /
- carbon dioxide /
- methanation
-
步学朋, 王鹏, 忻仕河, 梁大明, 戢绪国. 煤炭气化多联产生产代用天然气分析[J]. 煤化工, 2007, (6):4-8. (BU Xue-peng, WANG Peng, XIN Shi-he, LIANG Da-ming, JI Xu-guo. Analysis of coal gasification/poly-generation to produce substitute natural gas(SNG)[J]. Coal Chemical Industry, 2007, (6):4-8.) DU G, LIM S, YANG Y, WANG C, PFEFFERLE L, HALLER G L. Methanation of carbon dioxide on Ni-incorporated MCM-41 catalysts:The influence of catalyst pretreatment and study of steady-state reaction[J]. J Catal, 2007, 249(2):370-379. KUSAMA H, BANDO K K, OKABE K, ARAKAWA H. Effect of metal loading on CO2 hydrogenation reactivity over Rh/SiO2 catalysts[J]. Appl Catal A, 2000, 197(2):255-268. TAKENAKA S, SHIMIZU T, OTSUKA K. Complete removal of carbon monoxide in hydrogen-rich gas stream through methanation over supported metal catalysts[J]. Int J Hydrogen Energy, 2004, 29(10):1065-1073. 赵刚炜, 肖云汉, 王钰. 煤制天然气工艺技术和催化剂影响因素的分析探讨[J]. 陶瓷, 2009, (11):21-25. (ZHAO Gang-wei, XIAO Yun-han, WANG Yu. Analysis and discussion of process coal based synthetic natural gas and the factors effecting the catalysts[J]. Ceramic, 2009, (11):21-25.) 徐霖, 于金华. 低温型甲烷化催化剂的研制[J]. 化肥工业, 2005, 32(3):13-16. (XU Lin, YU Jin-hua. Study of methanation catalysts at low temperature[J]. Fertilizer Industry, 2005, 32(3):13-16.) KUSTOV A L, FREY A M, LARSEN K E, JOHANNESSEN T, NΦRSKOV J K, CHRISTENSEN C H. CO methanation over supported bimetallic Ni–Fe catalysts:From computational studies towards catalyst optimization[J]. Appl Catal A, 2007, 320:98-104. DAGLE R A, WANG Y, XIA G-G, STROHM J J, HOLLADAY J, PALO R D. Selective CO methanation catalysts for fuel processing applications[J]. Appl Catal A, 2007, 326(2):213-218. SHI P, LIU C-J. Characterization of silica supported nickel catalyst for methanation with improved activity by room temperature plasma treatment[J]. Catal Lett, 2009, 133(1/2):112-118. PARK J N, MCFARLAND E W.A highly dispersed Pd-Mg/SiO2 catalyst active for methanation of CO2[J]. J Catal, 2009, 266(1):92-97. PHOLJAROEN B, LAOSIRIPOJANA N, PRASERTHDAM P, ASSABUMRUNGRAT S. Reactivity of Ni/SiO2·MgO toward carbon dioxide reforming of methane under steady state and periodic operations[J]. J Ind Eng Chem, 2009, 15(4):488-497. 莫欣满, 董新法, 刘其海, 林维明. 纳米ZrO2负载Ni催化剂催化CO选择性甲烷化[J]. 石油化工, 2008, 37(7):656-661. (MO Xin-man, DONG Xin-fa, LIU Qi-hai, LIN Wei-ming. Selective methanation of CO over Ni-based catalysts supported on nano-zirconia[J]. Petrochemical Technology, 2008, 37(7):656-661.) YAMASAKI M, HABAZAKI H, ASAMI K, IZUMIYA K, HASHIMOTO K. Effect of tetragonal ZrO2 on the catalytic activity of Ni/ZrO2 catalyst prepared from amorphous Ni-Zr alloys[J]. Catal Commun, 2006, 7(1):24-28. REZAEI M, ALAVI S M, SAHEBDELFAR S, BAI P, LIU X, YAN Z-F. CO2 reforming of CH4 over nanocrystalline zirconia-supported nickel catalysts[J]. Appl Catal B, 2008, 77(3/4):346-354. LIU Q H, DONG X F, LIN W M. Highly selective CO methanation over amorphous Ni-Ru-B/ZrO2 catalyst[J]. Chinese Chemical Letters, 2009, 20(8):889-892. ZHANG S, WANG J, WANG X. Effect of calcination temperature on structure and performance of Ni/TiO2-SiO2 catalyst for CO2 reforming of methane[J]. J Nat Gas Chem, 2008, 17(2):179-183. 钟顺和, 王希涛, 宓立新, 肖秀芬. ZrO2-SiO2负载Cu-Ni催化剂的CO2加氢反应性能[J]. 分子催化,2001, 15(3):170-176. (ZHONG Shun-he, WANG Xi-tao, MI Li-xin, XIAO Xiu-fen. Catalytic performance of ZrO2-SiO2 supported Ni-Cu alloy catalysts for CO2 hydrogenation[J]. Journal of Molecular Catalysis(China), 2001, 15(3):170-176.) RANA M S, MAITY S K, ANCHEYTA J, MURALI DHAR G, PRASADA RAO T S R. MoCo(Ni)/ZrO2-SiO2 hydrotreating catalysts:physico-chemical characterization and activities studies[J]. Appl Catal A, 2004, 268(1/2):89-97. HABAZAKI H, YAMASAKI M, ZHANG B P, KAWASHIMA A, KOHNO S, TAKAI T, HASHIMOTO K. Co-methanation of carbon monoxide and carbon dioxide on supported nickel and cobalt catalysts prepared from amorphous alloys[J]. Appl Catal A, 1998, 172(1):131-140. 梁开明, 顾扣芬, 顾守仁, 孙传水. ZTA陶瓷ZrO2的韧化机制与断裂特征[J]. 硅酸盐学报, 1995, 23(5):477-487. (LIANG Kai-ming, GU Ko-fen, GU Shou-ren, SUN Chuan-shui. Toughening mechanisms and fracture characteristics of ZrO2 in ZTA ceramics[J]. Jouranal of the Chinese Ceramic Society, 1995, 23(5):477-487.)
点击查看大图
计量
- 文章访问数: 1800
- HTML全文浏览量: 17
- PDF下载量: 1037
- 被引次数: 0