Preparation and mechanism of Fe-K/AC for catalytic oxidation of hydrogen sulfide
-
摘要: 采用正交实验法制备了负载铁、钾的活性炭(Fe-K/AC)热煤气催化氧化脱硫剂,考察了活性组分铁、钾含量、二价铁和三价铁比例、煅烧温度对催化氧化脱硫反应活性的影响。由正交实验极差分析可知,各因素影响程度依次为:钾含量>铁含量>煅烧温度> Fe2+/Fe3+,最优制备条件为,铁含量0.5%、钾含量5.0%、煅烧温度600 ℃、Fe2+/Fe3+比0.5。通过对脱硫剂的孔隙结构和表面形貌分析可知,活性炭表面负载的铁金属氧化物具有催化氧化硫化氢生成单质硫的活性,碱金属氧化物具有协同作用,可以改变表面酸碱性,促进硫化氢的催化转化,但过高的金属氧化物负载量会阻塞孔道,减小反应比表面积,从而降低脱硫剂的反应活性。Abstract: Modified activated carbon Fe-K/AC (activated carbon supported iron and potassium) was used as an oxidation catalyst for low concentration hydrogen sulfide (H2S) removed. The orthogonal design method was introduced in the research of Fe-K/AC preparation to determine the optimum condition and to measure the impact of different factors. Then, catalytic activity and mechanism on Fe-K/AC catalyst for oxidation of hydrogen sulfide was investigated. The optimum preparation condition of Fe-K/AC with high sulfur capacity and selectivity is that the iron and potassium content is 0.5% and 5.0%, respectively; and the calcination temperature and the Fe2+/Fe3+ atomic ratio is 600 ℃ and 0.5, respectively. The order of their influences is potassium content > iron content > calcination temperature > Fe2+/Fe3+ atomic ratio. Results from structural parameters and surface morphology of sorbents reveal that iron metal oxide loaded on the surface of activated carbon has the selective catalytic oxidation activity of hydrogen sulfide to element sulfur. Alkali metal oxide, which changes basic surface groups, has a synergistic effect on the catalytic oxidation of hydrogen sulfide. However,the catalytic activity decreases due to excessive metal oxides loadings that may block the accessibility of micropores and reduce the surface area.
-
Key words:
- Fe-K/AC /
- desulfurization /
- catalytic oxidation /
- hot coal gas /
- orthogonal design
-
李彦旭, 李春虎, 郭汉贤, 钟炳. 国内外高温煤气脱硫技术探讨[J]. 煤化工, 1998, (3):20-24. (LI Yan-xu, LI Chun-hu, GUO Han-xian, ZHONG Bing. On gas desulfurization at high temperature[J]. Coal Chemistry Industry, 1998, (3):20-24.) DROOG H A, DELWEL A, ASSINK R. Comparison of high temperature gas treatment options with low-temperature gas treatment in IGCC’s following entrained flow gasification//In:Proceedings 12th EPRI Conference on Gasification Power Plants. San Francisco:1993. BASHKOVA S, BAKER F S, WU X, ARMSTRONG T R, SCHWARTZ V. Activated carbon catalyst for selective oxidation of hydrogen sulphide:On the influence of pore structure, surface characteristics, and catalytically-active nitrogen[J]. Carbon, 2007, 45(6):1354-1363. NGUYEN-THANH D, BANDOSZ T J. Activated carbons with metal containing bentonite binders as adsorbents of hydrogen sulfide[J]. Carbon, 2005, 43(2):359-367. WU X, KERCHER A K, SCHWARTZ V, OVERBURY S H, ARMSTRONG T R. Activated carbons for selective catalytic oxidation of hydrogen sulfide to sulfur[J]. Carbon, 2005, 43(5):1087-1090. STEIJNS M, DERKS F, VERLOOP A, MARS P. The mechanisms of the catalytic oxidation hydrogen sulfide Ⅱ kinetics and mechanisms of hydrogen sulfide oxidation catalyzed by sulfur[J]. J Catal, 1976, 42(1):87-95. COSKUN I, TOLLEFSON E L. Oxidation of low concentrations of hydrogen sulfide over activated carbon[J]. Can J Chem Eng, 1980, 58(1):72-76. KONSHENKO E V, BALAEV A V, ISMAGILOV F R, SPIVAK S I, SAFIN R R. Direct catalytic oxidation of hydrogen sulfide[J]. Chem Technol Fuels Oils, 2001, 37(3):212-218. 谭小耀, 吴迪镛, 袁权. 浸渍活性炭脱除低浓度H2S的研究[J]. 化学工程, 1996, 24(6):21-25. (TAN Xiao-yao, WU Di-yong, YUAN Quan. Investigation of removal of low concentration hydrogen sulfide on impregnated activated carbon[J]. Chemical Engineering, 1996, 24(6):21-25.) 肖永厚, 王树东, 吴迪镛, 袁权. 浸渍活性炭脱除低质量浓度H2S性能的研究[J]. 燃料化学学报, 2007, 35(1):61-65. (XIAO Yong-hou, WANG Shu-dong, WU Di-yong, YUAN Quan. Investigation of removal of low concentration hydrogen sulfide on impregnated activated carbon[J]. Journal of Fuel Chemistry and Technology, 2007, 35(1):61-65.) YAN R, CHIN T, NG L Y, DUAN H, LIANG D T, TAY J H. Influence of surface properties on the mechanism of H2S removal by alkaline activated carbons [J]. Environ Sci Technol, 2004, 38(1):316-323. 马建蓉, 刘振宇, 郭世杰. 同时脱除烟气中硫和硝的V2O5/AC催化剂研究[J]. 燃料化学学报, 2005, 33(1):6-11. (MA Jian-rong, LIU Zhen-yu, GUO Shi-jie. Simultaneous removal of SO2 and NO by V2O5/AC catalyst[J]. Journal of Fuel Chemistry and Technology, 2005, 33(1):6-11.) 吴博, 黄戒介, 张荣俊, 赵建涛, 陈富艳, 王洋. 活性炭(焦)吸附催化脱除热煤气中硫化氢的研究[J]. 燃料化学学报, 2009, 37(3):355-359. (WU Bo, HUANG Jie-jie, ZHANG Rong-jun, ZHAO Jian-tao, CHEN Fu-yan, WANG Yang. Investigation of adsorption and catalytic removal of hydrogen sulfide on active carbon (char) in hot gas[J]. Journal of Fuel Chemistry and Technology, 2009, 37(3):355-359.) GARDNER T H, BERRY D A, LYONS K D, BEER S K, FREED A D. Fuel processor integrated H2S catalytic partial oxidation technology for sulfur removal in fuel cell power plants[J]. Fuel, 2002, 81(17):2157-2166. STEIJNS M, MARS P. The role of sulfur trapped in micropores in the catalytical partial oxidation of hydrogen sulfide with oxygen[J]. J Catal, 1974, 35(1):11-17. CAL M P, STRICKLER B W, LIZZIO A A, GANGWAL S K. High temperature hydrogen sulfide adsorption on activated carbon Ⅱ Effects of gas temperature, gas pressure and sorbent regeneration[J]. Carbon, 2000, 38(13):1767-1774. LAPERDRIX E, COSTENTIN G, SAUR O, LAVALLEY J C, NEDEZ C, SAVIN-PONCET S, NOUGAYREDE J. Selective oxidation of H2S over CuO/Al2O3:Identification and role of the sulfurated species formed on the catalyst during the reaction[J]. J Catal, 2000, 189(1):63-69. BAGREEV A, MENENDEZ J A, DUKHNO I, TARASENKO Y, BANDOSZ T J. Bituminous coal-based activated carbons modified with nitrogen as adsorbents of hydrogen sulfide[J]. Carbon, 2004, 42(3):469-476.
点击查看大图
计量
- 文章访问数: 1194
- HTML全文浏览量: 18
- PDF下载量: 1008
- 被引次数: 0