Preparation of MgFe-hydrotalcites and their catalytic performance in synthesis of biodiesel oil from chlorella protothecoides oil
-
摘要: 用改良尿素法制备了镁铁水滑石(MgFe-LDH),对其在小球藻油脂合成生物柴油反应中的催化性能进行了研究。利用XRD、FT-IR、SEM及FT-IR拟合、去卷积分析等技术对所制备的MgFe-LDH进行了表征,考察了pH值、Mg/Fe摩尔比、反应温度和时间对其结构和性能的影响。结果表明,Mg/Fe摩尔比为3或4、pH值为9.5,在110 ℃条件下反应10 h,所制备的MgFe-LDH(Mg3Fe或Mg4Fe)结晶度最高,粒径均匀,结构规整。与Mg/Fe摩尔比为2的MgFe-LDH(Mg2Fe)相比,Mg3Fe或Mg4Fe在完全分解焙烧时,其层板结构保持稳定,具有较高的晶体结晶度、较多的催化活性位和较高的催化活性。以Mg3Fe金属氧化物为催化剂,在醇/油摩尔比为6时反应1.5 h,生物柴油产率可达87%;该催化剂循环使用3次,仍具一定催化活性。Abstract: MgFe-hydrotalcites (MgFe-LDH) were prepared by using improved urea method and used as the catalysts in the synthesis of biodiesel oil from chlorella protothecoides oil. The hydrotalcites were characterized by XRD, FT-IR, SEM as well as Fourier self-deconvolution and band curve-fitting analyses; the effects of pH value, Mg/Fe mol ratio, temperature and time to prepare the hydrotalcites on their properties and catalytic performances were investigated. The results showed that the MgFe-LDH with Mg/Fe mol ratio of 3 and 4 (Mg3Fe and Mg4Fe), prepared at 110 ℃ and pH value of 9.5 for 10 h exhibits high symmetrical crystalline structure. The brucite-like layer of Mg3Fe and Mg4Fe hydrotalcites are stable under calcination for a completely decomposition. compared with the Mg2Fe hydrotalcite with Mg/Fe mol ratio of 2, Mg3Fe and Mg4Fe upon calcination exhibit higher crystallinity and more active sites and higher catalytic activity. For the synthesis of biodiesel oil from chlorella protothecoides oil over the Mg3Fe catalyst, with methanol/oil molar ratio of 6 in the feed, the biodiesel oil yield reaches 87% after reaction 1.5 h; the catalyst can be reused for three times without serious deactivation.
-
Key words:
- MgFe-hydrotalcite /
- chlorella protothecoides /
- biodiesel /
- deconvolution
-
CAVANI F, TRIFIRO F, VACCARI A. Hydrotalcite-type anionic clays: Preparation, properties and application[J]. Catal Today, 1991, 11(2): 173-301. 孟伟青, 李峰, EVANS D G. 硝酸根型镁铁水滑石的合成及其离子交换性能研究[J]. 现代化工, 2004, 24(3): 25-28. (MENG Jian-wei, LI Feng, EVANS D G. Preparation and anion-exchange of MgFe-NO- layered double hydroxides[J]. Modern Chemical Industry, 2004, 24(3): 25-28.) LIU J, LI F, EVANS D G, DUAN X. Stoichiometry synthesis of a pure ferrite from a tailored layered double hydroxides (hydrotalcite-like) precursors[J]. Chem Commun, 2003, (4): 542-543. 吴旭, 谢鲜梅, 杜亚丽. 水滑石类材料在氧化还原催化反应中的应用[J]. 工业催化, 2006, 14(3): 1-5. (WU Xu, XIE Xian-mei, DU Ya-li. Application of hydrotalcite-like materials in catalytic redox reactions[J]. Industrial Catalysis, 2006, 14(3): 1-5.) 葛欣, 王益, 沈俭一, 张惠良. 镁铁和镁铁铝催化剂氢还原过程的研究[J]. 无机化学学报, 2000, 16(1): 79-83. (GE Xin, WANG Yi, SHEN Jian-yi, ZHANG Hui-liang. Study of hydrogen reduct ion of Mg-Fe and Mg-Fe-Al oxide catalysts[J]. Chinese Journal of Inorganic Chemistry, 2000, 16(1): 79-83.) 钱俊峰, 王菲, 刘森, 云志. 棉籽现场碱催化转酯化联产生物柴油和无毒棉粕[J]. 燃料化学学报, 2009, 37(4): 438-443. (QIAN Jun-feng, WANG Fei, LIU Sen, YUN Zhi. Production of biodiesel and nontoxic cottonseed meal from the cottonseed by in-situ alkaline-catalyzed transesterification[J] Journal of Fuel Chemistry and Technology, 2009, 37(4): 438-443.) 邓欣, 曾虹燕, 冯震. 纳米晶镁铝水滑石制备机理及抗毒性研究[J]. 功能材料, 2007, 38(6): 965-971. (DENG Xin, ZENG Hong-yan, FENG Zhen. The preparation mechanism and anti-toxicity study on nanocrystalline Mg-Al hydrotalcite[J]. Journal of Functional Materials, 2007, 38(6): 965-971.) 李玉芹, 袁正求, 冯岳, 黎萍, 周蒙, 姚威, 张剑. 不同碳氮组合对小球藻异养培养油脂积累的影响[J]. 中国生物制品学杂志, 2010, 23(9): 1009-1013. (LI Yu-qin, YUAN Zheng-qiu, FENG Yue, LI Ping, ZHOU Meng, YAO Wei, ZHANG Jian. Effect of carbon and nitrogen sources on lipid accumulation of heterotrophic microalgae chlorella protothecoides[J]. Chinese Journal of Biologicals. 2010, 23(9): 1009-1013.) 颜芳, 袁振宏, 吕鹏梅, 罗文, 杨玲梅, 邓利. 亚铁锌双金属氰化络合物固体催化剂催化合成生物柴油[J]. 燃料化学学报. 2010, 38(3): 281-286. (YANG Fang, YUAN Zhen-hong, LV Peng-mei, LUO Wen, YANG Ling-mei, DENG Li. Synthesis of biodiesel by Fe(II)-Zn double-metal cyanide complexes[J]. Journal of Fuel Chemistry and Technology. 2010, 38(3): 281-286.) 陆军, 刘晓磊, 史文颖, 王心蕊, 卫敏, 段雪. 水滑石类插层组装功能材料[J]. 石油化工, 2008, 37(6): 539-547. (LU Jun, LIU Xiao-lei, SHI Wen-ying, WANG Xin-rui, WEI Min, DUAN Xue. Functional materials of intercalated assembling layered double hydroxides[J]. Petrochemical Technology, 2008, 37(6): 539-547.) CORDEIRO C S, ARIZAGA G G C, RAMOS L P, WYPYCH F. A new zinc hydroxide nitrate heterogeneous catalyst for the esterification of free fatty acids and the transesterification of vegetable oils[J]. Catal Commun, 2008, 9(11/12): 2140-2143. LI E, XU Z P, RUDOLPH V. MgCoAl-LDH derived heterogeneous catalysts for the ethanol transesterification of canola oil to biodiesel[J]. Appl Catal B, 2009, 88(1/2): 42-49. 黄炎, 曾虹燕, 王亚举, 杨永杰, 魏英民, 赵策. 尿素法合成镁铁水滑石制备机理[J]. 硅酸盐学报, 2011, 39(2): 365-370. (HUANG Yan, ZENG Hong-yan, WANG Ya-ju, YANG Yong-jie, WEI Ying-min, ZHAO Ce. Preparation mechanism of the Mg-Fe hydrotalcite with urea method[J]. Journal of the Chinese ceramic society, 2011, 39(2): 365-370.) 张慧, 齐荣, 段雪. 镁铁和镁铝双羟基复合金属氧化物的结构和性能差异[J]. 无机化学学报, 2002, 18(8): 833-838. (ZHANG Hui, QI Rong, DUAN Xue. Studies on structures and properties of MgAl and MgFe layered double hydroxides[J]. Chinese Journal of Inorganic Chemistry, 2002, 18(8): 833-838.) KLOPROGGE J T, FROST R L. Fourier transform infrared and Raman spectroscopic studyof the local structure of Mg-, Ni-, and Co-hydrotalcites[J]. J Solid State Chem, 1999, 146(2): 506-515.
点击查看大图
计量
- 文章访问数: 1502
- HTML全文浏览量: 20
- PDF下载量: 853
- 被引次数: 0