Catalytic performance of La-Mn-Fe-Cu/HZSM-5 catalysts for soot combustion from diesel exhaust
-
摘要: 采用柠檬酸络合浸渍法制备分子筛负载钙钛矿型金属复合氧化物催化剂。采用XRD、SEM、XPS和H2-TPR等手段对催化剂性能进行表征,并在微型固定床反应器中对催化剂进行活性评价。结果表明,B位离子由多种金属离子组成的催化剂,可使碳颗粒燃烧温度降低,生成CO2的选择性高。B位离子种类及配比直接影响催化剂性能,Cu离子加入可提高生成CO2的选择性,Co离子加入可降低碳颗粒燃烧温度,调节Fe/Mn离子摩尔比可以改善碳颗粒燃烧温度和生成CO2的选择性。其中,LaMn0.2Fe0.7Cu0.1O3/HZSM-5催化剂性能较好,碳颗粒燃烧温度较低,Tig、Tm和Tf分别为236.6、419.0和458.7 ℃,生成CO2选择性较高,为88.3%。Abstract: The catalysts of perovskite-type complex oxide loaded on HZSM-5 zeolite were synthesized. The catalysts were characterized by XRD, SEM, XPS and H2-TPR, and their performance for combusting soot was evaluated in a fixed micro-reactor. The results show that when B-site ion was consisted of various metals, the catalytic performance was improved, the soot combustion temperature decrease, and the selectivity forming CO2 increased. The performance of catalysts was affected by the species and component of B-site ion. The selectivity forming CO2 increased and the temperature of soot combustion reduced when Cu and Co ion was in B-site, respectively. The temperature of soot combustion and selectivity forming CO2 was improved with changing the mole ratio of Fe/Mn. Among them, LaMn0.2Fe0.7Cu0.1O3/HZSM-5 catalyst has better performance with lower combustion temperature of Tig, Tm and Tf at 236.6, 419.0 and 458.7 ℃, respectively, and higher selectivity forming CO2 of 88.3%。
-
Key words:
- perovskite-type complex oxide /
- HZSM-5 /
- soot /
- catalytic combustion
-
ATRIBAK I, BUENO-LPEZ A, GARCÍA-GARCÍA A. Combined removal of diesel soot particulates and NOx over CeO2-ZrO2 mixed oxides[J]. J Catal, 2008, 259(1): 123-132. WU X, LIN F, WENG D, LI J. Simultaneous removal of soot and NO over thermal stable Cu-Ce-Al mixed oxides[J]. Catal Commun, 2008, 9(14): 2428-2432. ZHAO B, WANG R, YANG X. Simultaneous catalytic removal of NOx and diesel soot particulates over La1-xCexNiO3 perovskite oxide catalysts[J]. Catal Commun, 2009, 10(7): 1029-1033. WANG H, ZHAO Z, XU C-M, LIU J. Nanometric La1-xKxMnO3 perovskite-type oxides ——highly active catalysts for the combustion of diesel soot particle under loose contact conditions[J]. Catal Lett, 2005, 102(3/4): 251-255. ZHANG G, ZHAO Z, LIU J, XU J, JING Y, DUAN A, JIANG G. Macroporous perovskite-type complex oxide catalysts of La1-xKxCo1-yFeyO3 for diesel soot combustion[J]. J Rare Earths, 2009, 27(6): 955-960. WANG K, QIAN L, ZHANG L, LIU H, YAN Z. Simultaneous removal of NOx and soot particulates over La0.7Ag0.3MnO3 perovskite oxide catalysts[J]. Catal Today, 2010, 158(3/4): 423-426. TERAOKA Y, KANADA K, KAGAWA S. Synthesis of La-K-Mn-O perovskite-type oxides and their catalytic property for simultaneous removal of NOx and diesel soot particulates[J]. Appl Catal B, 2001, 34(1): 73-78. WANG H, ZHAO Z, XU C-M, LIU J. Highly active La1-xKxCoO3 perovskite complex oxide catalysts for the simultaneous removal of diesel soot and nitrogen oxides under loose contact conditions[J]. Catal Lett, 2008, 124(1/2): 91-99. 侯岩峰, 范国梁, 宋崇林, 黄齐飞, 张仲荣. La1-xexCoO3系钙钛矿型催化剂应用于柴油机尾气净化催化性能的研究[J]. 燃料化学学报, 2006, 34(1): 85-90. (HOU Yan-feng, FAN Guo-liang, SONG Chong-lin, HUANG Qi-fei, ZHANG Zhong-rong. Study on properties of La1-xCexCoO3 system perovskite-type catalysts for diesel engine exhaust removal[J]. Journal of Fuel Chemistry and Technology, 2006, 34(1): 85-90.) 陈广新, 余林, 林永强, 王明强. La-Sr-Fe-Co系钙钛矿型汽车尾气净化催化剂的性能研究[J]. 分子催化, 2005, 19(4): 206-265. (CHEN Guang-xin, YU Lin, LIN Yong-qiang, WANG Ming-qiang. The investigation of catalytic activity of La-Sr-Fe-Co perovskite-type-oxide[J]. Journal of Molecular Catalysis(China), 2005, 19(4): 206-265.) 彭小圣, 林赫, 黄震,上官文峰. 采用钙钛矿型催化剂(La0.8 K0.2Cu0.05Mn0.5O3 )同时催化去除NOx和碳烟的研究[J]. 环境科学学报, 2006, 26(5): 779-784. (PENG Xiao-sheng, LIN He, HUANG Zhen, SHANGGUAN Wen-feng. Investigation of catalytic removal of NOx and soot over La0.8K0.2Cu0.05Mn0.95O3[J]. Acta Scientiae Circumstantiae, 2006, 26(5): 779-784.) 彭小圣, 林赫, 黄震, 上官文峰. La-Mn-O钙钛矿催化剂成分对NOx和碳烟同时催化去除的影响[J]. 高校化学工程学报, 2006, 20(5): 831-836. (PENG Xiao-sheng, LIN He, HUANG Zhen, SHANGGUAN Wen-feng. Influence of composition of perovskite-type catalysts La1-xAxByMn1-yO3 on simultaneous removal of NOx and soot[J]. Journal of Chemical Engineering of Chinese Universities, 2006, 20(5): 831-836.) ZHAO Z, YANG X, WU Y. Comparative study of nickel-based perovskite-like mixed oxide catalysts for direct decomposition of NO[J]. Appl Catal B, 1996, 8(3): 281-297. 傅希贤, 杨秋华, 桑丽霞. 钙钛矿型LaFe1-xCuxO3的光催化活性研究[J]. 高等学校化学学报, 2002, 23(2): 283-286. (FU Xi-xian, YANG Qiu-hua, SANG Li-xia. Studies on photocatalytic activity of perovskite type LaFe1-xCuxO3[J]. Chemical Research in Chinese Universities, 2002, 23(2): 283-286.) 丁铁柱, 其其格, 李健, 季秉厚. 稀土氧化物LSCO/YSZ的XRD和XPS研究[J]. 中国稀土学报, 2002, 20(4): 320-323. (DING Tie-zhu, QI Qi-ge, LI Jian, JI Bin-hou. XRD and XPS studies on rare earth oxide LSCO/YSZ electrodes[J]. Journal of the Chinese Rare Earth Society, 2002, 20(4): 320-323.)
点击查看大图
计量
- 文章访问数: 1622
- HTML全文浏览量: 13
- PDF下载量: 869
- 被引次数: 0