Study on iron-manganese catalysts for Fischer-Tropsch synthesis
-
摘要: Iron-manganese catalysts were prepared by co-precipitation method. Characterization of catalysts was carried out by using X-ray diffraction (XRD), scanning electron microscopy (SEM), temperature program reduction (TPR), N2 adsorption-desorption measurements. The results from catalytic performance tests in Fischer-Tropsch synthesis showed that the iron-manganese catalysts are supersensitive to catalyst composition and materials source. It was found that C2~4 light olefins increased while CH4 and CO2 decreased by using iron-manganese catalyst prepared from iron (Ⅱ) sulfate (A catalyst). The activity and selectivity of A catalyst was studied in different operational conditions. The results showed that the best operational conditions for C2~4 light olefins production were H2/CO=1/1 (GHSV=2 400 h-1) at 260 ℃ under 0.3 MPa total pressure.Abstract: Iron-manganese catalysts were prepared by co-precipitation method. Characterization of catalysts was carried out by using X-ray diffraction (XRD), scanning electron microscopy (SEM), temperature program reduction (TPR), N2 adsorption-desorption measurements. The results from catalytic performance tests in Fischer-Tropsch synthesis showed that the iron-manganese catalysts are supersensitive to catalyst composition and materials source. It was found that C2~4 light olefins increased while CH4 and CO2 decreased by using iron-manganese catalyst prepared from iron (Ⅱ) sulfate (A catalyst). The activity and selectivity of A catalyst was studied in different operational conditions. The results showed that the best operational conditions for C2~4 light olefins production were H2/CO=1/1 (GHSV=2 400 h-1) at 260 ℃ under 0.3 MPa total pressure.
-
CLAEYS M, van STEEN E. Fischer-Tropsch Technology[M]. Stud Surf Sci Catal, 2004, 152: 601-680. SARKAR A, SETH D, DOZIER A K, NEATHERY J K, HAMDEH H H, DAVIS B H. Fischer-Tropsch synthesis: Morphology, phase transformation and particle size growth of nano-scale particles[J]. Catal Lett, 2007, 117(1/2): 1-17. POUR A N, TAGHIPOOR S, SHEKARRIZ M, SHAHRI S M K, ZAMANI Y. Fischer-Tropsch synthesis with Fe/Cu/La/SiO2 catalyst[J]. J Nanosci Nanotechnol, 2009, 9(7): 4425-4429. HERRANZ T, ROJAS S, PEREZ-ALONSO F J, OJEDA M, TERREROS P, FIERRO J L G. Hydrogenation of carbon oxides over promoted Fe-Mn catalysts prepared by the microemulsion methodology[J]. Appl Catal A, 2006, 311: 66-75. POUR A N, HOUSAINDOKHT M R, TAYYARI S T, ZARKESH J. Effect of nano-particle size on product distribution and kinetic parameters of Fe/Cu/La catalyst in Fischer-Tropsch synthesis[J]. J Nat Gas Chem, 2010, 19(2): 107-116. ERIKSSON S, NYLEN U, ROJAS S, BOUTONNET M. Preparation of catalysts from microemulsions and their applications in heterogeneous catalysis[J]. Appl Catal A, 2004, 265(2): 207-219. SCHWUGER M-J, STICKDORN K, SCHOMAECKER R. Microemulsions in technical processe[J]. Chem Rev, 1995, 95(4): 849-864. LIU C, ZOU B, RONDINONE A J, ZHANG Z J. Reverse micelle synthesis and characterization of superparamagnetic MnFe2O4 spinel ferrite nanocrystallites[J]. J Phys Chem B, 2000, 104(6): 1141-1145. FEYZI M, MIRZAEI A A. Performance and characterization of iron-nickel catalysts for light olefin production[J]. J Nat Gas Chem, 2010, 19(4): 422-430. FEYZI M, MIRZAEI A A, BOZORGZADEH H R. Effects of preparation and operation conditions on precipitated iron nickel catalysts for Fischer-Tropsch synthesis[J]. J Nat Gas Chem, 2010, 19(3): 341-353. Van den BERG F R, CRAJE M W J, van der KRAAN A M, GEUS J W. Reduction behaviour of Fe/ZrO2 and Fe/K/ZrO2 Fischer-Tropsch catalysts[J]. Appl Catal A, 2003, 242(2): 403-416. ANDERSON J R. Catalysis science and technology. vol. 1[M]. Springer, New York: Springer-Verlag Press, 1981. KING D L, CUSUMANO J A, GARTEN R L. A technological perspective for catalytic processes based on synthesis gas[J]. Catal Rev, 1981, 23(1/2): 233-263. MAITI G C, MALESSA R, BAERNS M. Iron/manganese oxide catalysts for Fischer-Tropsch synthesis: Part I Structural and textural changes by calcination, reduction and synthesis[J]. Appl Catal, 1983, 5(2): 151-170. MALESSA R, BAERNS M. Iron/manganese oxide catalysts for Fischer-Tropsch synthesis: 4 Activity and selectivity[J]. Ind Eng Chem Res, 1988, 27(2): 279-283. KOLBEL H, TILLMETZ K D. Process for the production of hydrocarbons and oxygen-containing compounds and catalysts therefore: US, 4177203[P].1979-12-04. DAS C K, DAS N S, CHOUDHURY D P, RAVICHANDRAN G, CHAKRABARTY D K. Hydrogenation of carbon monoxide on unsupported Fe-Mn-K catalysts for the synthesis of lower alkenes: Promoter effect of manganese[J]. Appl Catal A, 1994, 111(2): 119–132. Van der LAAN G P, BEENACKERS A A C M. Kinetics and selectivity of the Fischer-Tropsch synthesis: A literature review[J]. Catal Rev, 1999, 41(3/4): 255-318. GONZALEZ-CORTES S L, A RODULFO-BAECHLER S M, OLIVEROS A, OROZCO J, FONTAL B, MORA A J, DELGADO G. Synthesis of light alkenes on manganese promoted iron and iron-cobalt Fischer-Tropsch catalysts[J]. React Kinet Catal Lett, 2002, 75(1): 3-12. LI J, COVILLE N J. Effect of boron on the sulfur poisoning of Co/TiO2 Fischer-Tropsch catalysts[J]. Appl Catal A, 2001, 208(1/2): 177-184. YAMADA M, KOIZUMI N, MIYAZAWA A, FURUKAWA T. Novel catalytic properties of Rh sulfide for the synthesis of methanol from CO+H2 in the presence of H2S[J]. Catal Lett, 2002, 78(1/4): 195-199. BECK J, HILBERTT T . Ein altes' Rhodiumsulfid mit überraschender struktur: Synthese, kristallstruktur und elektronische eigenschaften von Rh3S4[J]. Chemie, 2000, 626: 72-79. LI T, YANG Y, ZHANG C, AN X, WAN H, TAO Z, XIANG H, LI Y, YI F, XU B. Effect of manganese on an iron-based Fischer-Tropsch synthesis catalyst prepared from ferrous sulfate[J]. Fuel, 2007, 86(7/8): 921-928. STENGER H G, SATTERFIELD C N. Effect of liquid composition on the slurry Fischer-Tropsch synthesis: 2 Product selectivity[J]. Ind Eng Chem Process Des Dev, 1985, 24(2): 411-415. Van der KRAAN A M, RAMSELAAR W L T M, de BEER V H J. Mossbauer spectroscopy applied to inorganic chemistry, Vol. 3[M]// LONG G J, GRANDJEAN F. New York: Plenum Press, 1989: 376. FEYZI M, IRANDOUST M, MIRZAEI A A. Effects of promoters and calcination conditions on the catalytic performance of iron–manganese catalysts for Fischer–Tropsch synthesis[J]. Fuel Process Technol, 2011, 92(5): 1136-1143. BARRAULT J, FORQUY C, PERRICHON V. Effects of manganese oxide and sulphate on olefin selectivity of iron supported catalysts in the Fischer-Tropsch reaction[J]. Appl Catal, 1983, 5(1): 119-125. KITZELMANN D, VIELSTICH W. In-situ study of the primary reactions in the hydrogenation of CO on Fe-catalysts Fischer-Tropsch synthesis[J]. Z Phys Chem, 1978, 112(2): 215-233. MIRZAEI A A, HABIBPOUR R, KASHI E. Preparation and optimization of mixed iron cobalt oxide catalysts for conversion of synthesis gas to light olefins[J]. Appl Catal A, 2005, 296(2): 222-231. HUTCHINGS G J, MIRZAEI A A, JOYNER R W, SIDDIQUI M R H, TAYLOR S H. Effect of preparation conditions on the catalytic performance of copper manganese oxide catalysts for CO oxidation[J]. Appl Catal A, 1998, 166(1): 143-152. WHITTLE D M, MIRZAEI A A, HARGREAVES J S J, JOYNER R W, KIELY C J, TAYLOR S H, HUTCHINGS G J. Co-precipitated copper zinc oxide catalysts for ambient temperature carbon monoxide oxidation: Effect of precipitate ageing on catalyst activity[J]. Phys Chem Chem Phys, 2002, 4(23): 5915-5920. GONZALES-CORTES S L, RODULFO-BAECHLER M A, OROZCO J. Characterization of Fe-Co-Mn catalysts after carbon monoxide hydrogenation[J]. Rev Mex Fis, 2003, 49S3: 204-206. MADON R J, TAYLOR W F. Effect of sulfur on the Fischer-Tropsch synthesis alkali-promoted precipitated cobalt-based catalyst[M]. Adv Chem Ser, 1979, 178: 93-111. GRIBOVAL-CONSTANT A, KHODAKOV A Y, BECHARA R, ZHOLOBENKO V L. Support mesoporosity: A tool for better control of catalytic behavior of cobalt supported Fischer- Tropsch catalysts[M]. Stud Surf Sci Catal, 2002, 144: 609-616.
点击查看大图
计量
- 文章访问数: 1445
- HTML全文浏览量: 11
- PDF下载量: 937
- 被引次数: 0