Preparation and catalytic performance of FAU-type zeolite films supported on FeCrAl grids
-
摘要: 采用水热法制备FeCrAl丝网负载FAU沸石膜,考察了合成液老化、载体预涂晶种以及晶种液中添加聚乙烯醇(PVA)等因素的影响,评价了FeCrAl丝网负载FAU沸石膜对模型吸热燃料正辛烷裂解的催化活性。结果表明,载体表面预涂Y分子筛晶种后有助于增加载体表面分子筛负载量,采用老化后的合成液,效果更显著,并且更易在金属丝上生长出一层连续致密的FAU沸石膜。在相同水热合成条件下,载体表面用含PVA的晶种液预涂晶种后,可增加分子筛负载量。正辛烷在FeCrAl丝网负载FAU沸石膜上的初始裂解转化率(7.2%~13.2%,500 ℃)高于其在空白载体上的裂解转化率(4.4%),FAU沸石膜的初始催化活性不仅与载体表面分子筛负载量有关,也与分子筛膜的形貌有关。Abstract: The preparation of FAU-type zeolite films on FeCrAl grids by hydrothermal synthesis was studied with an emphasis on effects of ageing of the synthesis mixture, seeding of the support and addition of polyvinyl alcohol (PVA) in the seed solution. The catalytic activity of FAU-type zeolite films was evaluated for cracking of a model endothermic fuel (n-octane). The results show that coating of the support with Y-type zeolite seeds could increase the loading of zeolite crystals on the support and thus facilitate to grow a continuous and dense FAU-type zeolite film around the wire, especially using an aged synthesis mixture. Under the same synthesis conditions, the loading of zeolite crystals was enhanced using a PVA-containing seed solution for seeding. The initial conversion of n-octane at 500 ℃ was higher over FAU-type zeolite films (7.2%~13.2%) than that over the bare support (4.4%). The activity of zeolite films depends on not only the loading of zeolite crystals but also the morphology of the film.
-
Key words:
- FAU-type zeolite films /
- FeCrAl grids /
- catalytic cracking /
- endothermic fuel
-
LANDER H, NIXON A C. Endothermic fuels for hypersonic vehicles[J]. J Aircraft, 1971, 8(4): 200-207. 何龙, 潘富敏, 林瑞森. 吸热型碳氢燃料催化裂解的研究述评[J]. 推进技术, 2001, 22(2): 97-100. (HE Long, PAN Fu-min, LIN Rui-sen. Review of catalytic cracking of endothermic hydrocarbon fuel[J]. J Propulsion Technology, 2001, 22(2): 97-100.) 付全军, 燕珂, 杜宗罡, 李宁. 吸热型碳氢燃料研究进展[J]. 火箭推进, 2005, 31(5): 32-36. (FU Quan-jun, YAN Ke, DU Zong-gang, LI Ning. Research progress of endothermic hydrocarbon fuels[J]. J Rocket Propulsion, 2005, 31(5): 32-36.) 贺芳, 米镇涛, 孙海云. 提高烃类燃料热沉的研究进展[J]. 化学进展, 2006, 18(7/8): 1041-1048. (HE Fang, MI Zhen-tao, SUN Hai-yun. Improvement of heat sink of endothermic hydrocarbon fuels[J]. Progress in Chemistry, 2006, 18(7/8): 1041-1048.) SOBEL D R, SPADACCINI L J. Hydrocarbon fuel cooling technologies for advanced propulsion[J]. ASME J Eng Gas Turbines Power, 1997, 119(2): 344-351. HUANG H, SPADACCINI L J, SOBEL D R. Fuel-cooled thermal management for advanced aeroengines[J]. ASME J Eng Gas Turbines Power, 2004, 126(2): 284-293. 李佳, 邹吉军, 张香文, 郭伟, 米镇涛. 吸热燃料在管式涂层反应器内的催化裂解反应[J]. 石油化工, 2007, 36(4): 328-333. (LI Jia, ZOU Ji-jun, ZHANG Xiang-wen, GUO Wei, MI Zhen-tao. Catalytic cracking of endothermic fuels in coated tube reactor[J]. Petrochemical Technology, 2007, 36(4): 328-333.) 厉刚, 郑少烽, 孙聪明, 蔡尚立, 方文军, 林瑞森. JP-10燃料在HZSM-5/不锈钢筛网复合膜上的常压催化裂解[J]. 推进技术, 2009, 30(3): 375-379. (LI Gang, ZHENG Shao-feng, SUN Cong-ming, CAI Shang-li, FANG Wen-jun, LIN Rui-sen. Catalytic cracking of JP-10 at atmospheric pressure on HZSM-5/stainless-steel-grid film catalyst[J]. J Propulsion Technology, 2009, 30(3): 375-379.) 孙国锋, 刘垚, 鲁金明, 王金渠. 小晶粒FAU型沸石膜的液态导向合成及其渗透蒸发性能的研究[J]. 石油化工, 2008, 37(10): 1009-1014. (SUN Guo-feng, LIU Yao, LU Jin-ming, WANG J. Synthesis of small crystal FAU-type zeolite membrane by liquid directing-agent method and its pervaporation properties[J]. Petrochemical Technology, 2008, 37(10): 1009-1014.) JEONG B, SOTOWA K, KUSAKABE K. Catalytic dehydrogenation of cyclohexane in an FAU-type zeolite membrane reactor[J]. J Membr Sci, 2003, 224(1/2): 151-158. ZHU G, LI Y, ZHOU H, LIU J, YANG W. Microwave synthesis of high performance FAU-type zeolite membranes: Optimization, characterization and pervaporation dehydration of alcohols[J]. J Membr Sci, 2009, 337(1/2): 47-54. SATO K, SUGIMOTO K, SEKINE Y, TAKADA M, MATSUKATA M, NAKANE T. Application of FAU-type zeolite membranes to vapor/gas separation under high pressure and high temperature up to 5 MPa and 180 ℃[J]. Microporous Mesoporous Mater, 2007, 101(1/2): 312-318. KIM Y C, JEONG J Y, HWANG J Y, KIM S D, KIM W J. Influencing factors on rapid crystallization of high silica nano-sized zeolite Y without organic template under atmospheric pressure[J]. J Porous Mater, 2009, 16(3): 299-306. TREACY M M J, HIGGINS J B. Collection of simulated XRD powder patterns for zeolites[M]. 4th Ed. Amsterdam: Elsevier, 2001: 148-149.
点击查看大图
计量
- 文章访问数: 1923
- HTML全文浏览量: 20
- PDF下载量: 604
- 被引次数: 0