Changes in the microstructure and gasification reactivity of petroleum coke and coal samples after rapid pyrolysis
-
摘要: 为了研究在接近工业气化条件下石油焦和煤的结构和气化活性变化规律的差异,在滴管炉装置内,800~1 400℃对两种石油焦和一种烟煤进行快速热处理。用比表面积孔隙分析仪、XRD分析仪考察快速热处理对石油焦和煤的孔隙结构、碳微晶结构的影响,用热重分析仪考察不同温度快速热处理后石油焦和煤的CO2气化活性。结果表明,石油焦与煤相比,孔隙结构主要由微孔组成,随快速热处理温度的升高,石油焦和煤微孔比表面积和孔容均先增大后逐渐减小;快速热处理降低了石油焦和煤的石墨化程度,石油焦碳微晶结构变化主要表现在堆垛高度的变化,而煤的碳微晶结构变化在衍射峰对应的2θ002值、晶面间距和堆垛高度上均有体现;石油焦和煤的气化活性随快速热处理温度升高的变化趋势不同,但均与碳微晶结构参数(石墨化程度)的变化紧密相关。Abstract: To investigate the changes in the structure of petroleum coke and coal after rapid pyrolysis under the condition similar to the practical coal gasifier, two kinds of petroleum cokes and one bituminous coal were pyrolyzed in a drop tube furnace at 800~1 400℃. The structure of petroleum coke and coal were characterized by using surface area porosity analyzer and XRD (X-ray diffraction) analyzer, the CO2 gasification reactivity of samples was examined by TGA (thermogravimetric analyzer). The result shows that the pore in petroleum coke is mainly micropore compared with coal; with the increase of pyrolysis temperature, the micropore surface area of petroleum coke and coal increases first and then decreases gradually. Rapid pyrolysis lowers the graphitization degree of petroleum coke and coal. The changes in the carbon crystallite structure for petroleum coke are mainly observed in the average stacking height, while the changes in the carbon crystallite structure for coal is manifested in the value of 2θ002, interlayer spacing and average stacking height. Although the gasification reactivity changing tendency of petroleum coke and coal with the increase of pyrolysis temperature is different, the gasification reactivity is closely related to the carbon crystallite structure.
-
NAKAMURA D. Global refining capacity increases slightly in 2006[J]. Oil Gas J,2006,104(47): 56-62. 王玉章, 申海平, 刘自宾. 延迟焦化石油焦及应用[J]. 炼油技术与工程,2008,38(2): 25-30. (WANG Yu-zhang,SHEN Hai-ping,LIU Zi-bin. Coke of delayed coking and its application[J]. Petroleum Refinery Engineering, 2008,38(2):25-30.) MILENKOVA K S, BORREGO A G, ALVAREZ D, XIBERTA J, MENENDEZ R. Devolatilisation behaviour of petroleum coke under pulverised fuel combustion conditions [J]. Fuel, 2003, 82(15/17): 1883-1891. HAENEL M W. Recent progress in coal structure research [J]. Fuel. 1992, 71(11): 1211-1223. 李庆峰, 房倚天, 张建民, 王洋, 时铭显, 孙国刚. 石油焦水蒸气气化反应特性[J]. 燃料化学学报, 2003, 31(3): 204-209. (LI Qing-feng, FANG Yi-tian, ZHANG Jian-min, WANG Yang, SHI Ming-xian,SUN Guo-gang. Steam gasification characteristics of petroleum coke[J]. Joural of Fuel Chemistry and Technology, 2003, 31(3): 204-209. ) 许桂英, 孙国刚. 生物质与石油焦共气化特性的研究[J]. 燃料化学学报, 2011,39(6): 438-453. (XU Gui-ying, SUN Guo-gang. Study on characterisitics of co-gasification of biomass and petroleum coke[J]. Journal of Fuel Chemistry and Technology, 2011, 39(6): 438-453.) 吴诗勇, 吴幼青, 顾菁, 张晓, 高晋生. 高温煅烧条件下石油焦和沥青焦的物理结构及其CO2气化特性[J].石油学报(石油加工), 2009, 25(2): 258-265. (WU Shi-yong, WU You-qing, GU Jing,ZHANG Xiao,GAO Jin-sheng. Physical structures and CO2 gasification characristics of petroleum coke at condition of high temperature calcination[J]. Acta Petrolei Sinica (Petroleum Processing Section),2009,25(2): 258-265. ) 唐黎华, 陈冬霞, 朱学栋, 吴勇强, 倪燕慧, 朱子彬. 石油焦高温气化反应性[J]. 燃料化学学报, 2005, 33(6): 32-36. (TANG Li-hua,CHEN Dong-xia,ZHU Xue-dong,WU Yong-qiang,NI Yan-hui,ZHU Zi-bi. Gasification reactivity of petroleum coke at high temperature [J]. Journal of Fuel Chemistry and Technology,2005,33(6): 32-36.) 刘鑫, 张保申, 周志杰, 许建良, 王辅臣. 高温热处理对石油焦结构及气化活性的影响[J]. 石油学报(石油加工)2011, 27(1): 132-137. (LIU Xin, ZHANG Baoshen, ZHOU Zhijie, XU Jianliang, WANG Fuchen. Structure changes and gasification activity of petroleum coke after heat treatment[J]. Acta Petrolei Sinica (Petroleum Processing Section), 2011, 27(1): 132-137.) LEGIN-KOLAR M, RADENOVIC' A, UGARKOVIC' D. Changes in structural parameters of different cokes during heat treatment to 2400℃[J]. Fuel, 1999, 78(13): 1599-1605. 周军, 张海, 吕俊福, 岳光溪. 高温下热解温度对煤焦孔隙结构的影响[J]. 燃料化学学报, 2007, 35(2): 155-159. (ZHOU Jun, ZHANG Hai, LU Jun-fu, YUE Guang-xi. Effect of pyrolysis temperature on porous structure of anthracite chars produced at high temperatures [J]. Journal of Fuel Chemistry and Technology. 2007, 35(2): 155-159.) 唐黎华, 吴勇强, 朱学栋, 朱子彬. 高温下制焦温度对煤焦气化活性的影响[J]. 燃料化学学报, 2002, 30(1): 16-20. (TANG Li-hua, WU Yong-qiang, ZHU Xue-dong, ZHU Zi-bin. Effect on char making temperature on char gasification activity in higher temperature[J]. Journal of Fuel Chemisttry and Technology, 2002, 30(1): 16-20.) LU L, SAHAJWALLA V, HARRIS D. Characteristics of chars prepared from various pulverized coals at different temperatures using drop-tube furnace[J]. Energy Fuels, 2000, 14(4): 869-876. 常海州, 蔡雪梅, 李改仙, 白官, 吕秀清. 不同还原程度煤显微组分堆垛结构表征[J]. 山西大学学报(自然科学版), 2008,31(2): 223-227. (CHANG Hai-zhou, CAI Xue-mei, LI Gai-xian, BAI Guan, LV Xiu-qing. Characterization for the stacking structure of coal macerals with different type reductivity[J]. Journal of Shanxi University(Nat.Sci.Ed), 2008, 31(2): 223-227.)
点击查看大图
计量
- 文章访问数: 1775
- HTML全文浏览量: 22
- PDF下载量: 763
- 被引次数: 0