Preparation of nano-solid based catalyst CaO@SiO2 for the transesterification of soybean oil to biodiesel
-
摘要: 采用溶胶-凝胶法合成CaO@SiO2固体碱催化剂,以聚苯乙烯有机聚合物为硬模板剂和以P123为软模板剂对CaO的微观形貌进行调控。并将其应用于大豆油与甲醇的酯交换制备生物柴油的反应体系中。通过对CaO@SiO2纳米固体碱催化剂进行X射线衍射(XRD)、扫描电子显微镜(SEM)、透射电镜(TEM)、CO2-TPD及N2的吸附-脱附(BET)表征发现,不仅制备得到了形貌归整的纳米固体颗粒,而且得到了CaO包裹在SiO2表面的核壳结构。进一步考察了不同的硅钙质量比、反应温度、催化剂的用量以及油醇物质的量比对生物柴油收率的影响,生物柴油的收率最高可以达到95.6%。Abstract: The CaO@SiO2 alkaline catalyst was prepared by sol-gel method that chooses polystyrene as hard template and P123 as soft template to control the microstructure. Furthermore, the prepared catalyst was applied to the transesterification of soybean and methanol. Also, the nano-solid based catalyst was characterized by X-ray diffraction (XRD), scanning electron microscopy (SEM), transmission electron microscopy (TEM), CO2-TPD and N2 absorption-desorption (BET). The results show that the catalyst possesses an ordered morphology and core-shell structure. In addition, the effect of the ratio of SiO2/CaO (mass ratio), reaction temperatures, catalyst dosages and the ratio of oil/methanol (mol ratio) on the yield of biodiesel was examined. Under the best reaction condition, the yield of biodiesel can reach 95.6%.
-
Key words:
- CaO /
- transesterification /
- biodiesel /
- nano-catalyst
-
表 1 CaO@5SiO2和CaO的BET分析和生物柴油收率
Table 1 BET analysis of CaO@5SiO2and CaO and biodiesel yield
Catalyst A /(m2·g-1) v /(cm3·g-1) Biodiesel yield w/% CaO@SiO2 2.626 5 0.004 851 95.6 CaO 2.197 1 0.004 191 91.8 -
[1] LI H, XIA S Q, LUO H J, MA P S.Experimental and computational study on the compatibility of biodiesel/diesel/methanol blended fuel[J].Fuel, 2016, 173:52-59. doi: 10.1016/j.fuel.2016.01.036 [2] TANMAY B, MANAS K K, SUDIP B.Palladium nanoparticle-graphitic carbon nitride porous synergistic catalyst for hydrogen evolution/oxidation reactions over a broad range of pH and correlation of its catalytic activity with measured hydrogen binding energy[J].ACS Catal, 2016, 6(3):1929-1941. doi: 10.1021/acscatal.5b02485 [3] ABDERRAHIM B, RODRIGO V, MERCEDES M, JOSE A.Effect of free fatty acids contents on biodiesel quality.Pilot plant studies[J].Fuel, 2016, 174:54-62. doi: 10.1016/j.fuel.2016.01.018 [4] AHMAD M, ASADOLAH A, SHAHIN R, ELNAZ B K.Energy and cost analyses of biodiesel production from waste cooking oil[J].Renewable Sustainable Energy Rev, 2014, 33:44-49. doi: 10.1016/j.rser.2014.01.067 [5] 李晓红, 靳福全.CaO/(Mg-Fe-O) 固体碱的制备及其酯交换催化活性研究[J].油脂化工, 2015, 40(7):55-59. http://www.cnki.com.cn/Article/CJFDTOTAL-ZYZZ201507013.htmLI Xiao-hong, JIN Fu-quan.Preparation of CaO/(Mg-Fe-O) solid base and its catalytic activity in transesterification[J].China Oils Fats, 2015, 40(7):55-59. http://www.cnki.com.cn/Article/CJFDTOTAL-ZYZZ201507013.htm [6] 张传峰, 赵静, 方文军, 郭永胜.纳米催化剂在碳氢燃料和生物柴油领域中的应用[J].石油学报, 2015, 31(2):418-425. http://www.cnki.com.cn/Article/CJFDTOTAL-SXJG201502027.htmZHANG Chuan-feng, ZHAO Jing, FANG Wen-jun, GUO Yong-sheng.Application of nanocatalyst in the fields of hydrocarbon fuel and biodiesel[J].Acta Pet Sin, 2015, 31(2):418-425. http://www.cnki.com.cn/Article/CJFDTOTAL-SXJG201502027.htm [7] NAVOT K, AMJAD A.Biodiesel production via ethanolysis of jatropha oil using molybdenum impregnated calcium oxide as solid catalyst[J].RSC Adv, 2015, 5(18):13285-13295. doi: 10.1039/C4RA14786C [8] 郑华艳, 李茜茜, 崔丽萍, 李忠.Ca/Al固体碱催化菜籽油制备生物柴油[J].燃料化学学报, 2012, 40(3):331-336. http://rlhxxb.sxicc.ac.cn/CN/abstract/abstract17905.shtmlZHENG Hua-yan, LI Xi-qian, CUI Li-ping, LI Zhong.Synthesis of biodiesel from rapeseed oil catalyzed by Ca/Al solid base[J].J Fuel Chem Technol, 2012, 40(3):331-336. http://rlhxxb.sxicc.ac.cn/CN/abstract/abstract17905.shtml [9] JOSHI G, RAWAT D S, LAMBA B Y, BISHT K K, KUMAR P, KUMAR N, KUMAR S.Transesterification of Jatropha and Karanja oils by using waste egg shell derived calcium based mixed metal oxides[J].Energy Convers Manage, 2015, 96:258-267. doi: 10.1016/j.enconman.2015.02.061 [10] SIOW H T, AMINUL I, TALAL Y, YUN H T.Transesterification of nannochloropsis oculata microalga's oil to biodiesel using calcium methoxide catalyst[J].Energy, 2014, 78:63-71. doi: 10.1016/j.energy.2014.07.045 [11] NEZAHAT B, NEBAHAT D, DIHAN M K.Transesterification of canola oil to biodiesel using calcium bentonite functionalized with K compounds[J].Appl Catal B:Environ, 2013, 138-139:236-242. doi: 10.1016/j.apcatb.2013.02.043 [12] 孙艳荣, 范涛, 刘峰, 马利国, 汪长安.模板剂对共沉淀法合成纳米羟基磷灰石粉体形貌的影响[J].硅酸盐学报, 2012, 40(1):90-94. http://www.cnki.com.cn/Article/CJFDTOTAL-GXYB201201016.htmSUN Yan-rong, FAN Tao, LIU Feng, MA Li-guo, WANG Chang-an.influence of templates on morphology of nano-hydroxyapatite synthesized by Co-precipitation method[J].J Chin Ceram Soc, 2012, 40(1):90-94. http://www.cnki.com.cn/Article/CJFDTOTAL-GXYB201201016.htm [13] 沈少春, 袁志庆, 杨为民, 李应成.新型双子季胺碱模板剂的合成及纳米ZSM-5分子筛的制备[J].工业催化, 2015, 23(10):763-766. http://www.cnki.com.cn/Article/CJFDTOTAL-GYCH201510006.htmSHEN Shao-chun, YUAN Zhi-qing, YANG Wei-min, LI Ying-cheng.Preparation of nano-sized ZSM-5 zeolite based on the novel template gemini quaternary ammonium hydroxide[J].Ind Catal, 2015, 23(10):763-766. http://www.cnki.com.cn/Article/CJFDTOTAL-GYCH201510006.htm [14] 汪亚运, 陈杨, 赵晓兵, 秦佳伟.抛光压力对PS/CeO2纳米复合磨粒抛光性能的影响[J].微纳电子技术, 2015, 52(2):129-134.WANG Ya-yun, CHEN Yang, ZHAN Xiao-bing, QIN Jia-wei.Effects of the polishing pressure on the polishing performance of nano-sized PS/CeO2 composite abrasives[J].Micronanoelectron Technol, 2015, 52(2):129-134. [15] RASHAD M M, IBRAHIM I A.Improvement of the magnetic properties of barium hexaferrite nanopowders using modified co-precipitation method[J].J Mang Magn Mater, 2011, 323(16):2158-2164. doi: 10.1016/j.jmmm.2011.03.023 [16] 欧阳密, 黄森彪, 韩延刚, 吕晓静, 杨媛, 戴玉玉, 吕耀康, 张诚.以氨基化的聚苯乙烯微球为模板制备电致变色性能优良的单层有序多孔PBTB薄膜[J].物理化学学报, 2015, 31(3):476-482. http://www.cnki.com.cn/Article/CJFDTOTAL-WLHX201503011.htmOU Yang-mi, HUANG Sen-biao, HAN Yan-gang, LV Xiao-jing, YANG yuan, DAI Yu-yu, LU Yao-kang, ZHANG Cheng.Enhanced electrochromic performance of ordered porous monolayer PBTB film using amine-modified polystyrene spheres as a template[J].Acta Phys-Chim Sin, 2015, 31(3):476-482. http://www.cnki.com.cn/Article/CJFDTOTAL-WLHX201503011.htm [17] XIE W L, YANG X L, FAN M L.Novel solid base catalyst for biodiesel production:Mesoporous SBA-15 silica immobilized with 1, 3-dicyclohexyl-2-octylguanidine[J].Renewable Energy, 2015, 80:230-237. doi: 10.1016/j.renene.2015.02.014 [18] 侯谦奋, 张前前, 郭华荣, 李苓.CaO/SBA-15固体碱催化剂的合成表征及其催化餐饮废油制备生物柴油的研究[J].化学与生物工程, 2015, 32(8):28-34. http://www.cnki.com.cn/Article/CJFDTOTAL-HBHG201508007.htmHOU Qian-fen, ZHANG Qian-qian, GUO Hua-rong, LI Ling.Synthesis and characterization of Ca/SBA-15 solid base catalyst and its application in biodiesel production via waste cooking oil[J].Chem Bioeng, 2015, 32(8):28-34. http://www.cnki.com.cn/Article/CJFDTOTAL-HBHG201508007.htm [19] 侯丽伟, 易玉峰, 丁福臣.高碘酸氧化法测定甘油含量影响因素研究[J].粮食与油脂, 2010, (1):36-40. http://www.cnki.com.cn/Article/CJFDTOTAL-LSYY201001015.htmHOU Li-wei, YI Yu-feng, DING Fu-chen.Study on affecting factors of determining glycerol content with periodic acid oxidation[J].Cereal Oil, 2010, (1):36-40. http://www.cnki.com.cn/Article/CJFDTOTAL-LSYY201001015.htm [20] 郭萍梅, 黄庆.生物柴油中游离甘油和总甘油测定方法研究[J].粮食与油脂, 2003, (8):41-42. http://www.cnki.com.cn/Article/CJFDTOTAL-LSYY200308017.htmGUO Ping-mei, HUANG Qing.Study on analytical method of free glycerin and total glycerin in biodiesel[J].Cereal Oil, 2003, (8):41-42. http://www.cnki.com.cn/Article/CJFDTOTAL-LSYY200308017.htm [21] PUNNAMA S, SHIGEO H, ATSUO Y, KYIOSHI O.Preparation and sintering of CaSiO3 from coprecipitated powder using NaOH as precipitant and its apatite formation in simulated body fluid solution[J].J Mater Res, 1999, 14(2):529-536. doi: 10.1557/JMR.1999.0076 [22] JIANG W, NIU X Y, YUAN F L, ZHU Y J, FU H G.Preparation of KF-La2O2CO3 solid base catalysts and their excellent catalytic activities for transesterification of tributyrin with methanol[J].Catal Sci Technol, 2014, 4:2957-2968. doi: 10.1039/C4CY00167B [23] 范明明, 刘延磊, 张萍波, 蒋平平.CaO-MgO@CoFe2O4磁性固体碱的制备及其大豆油酯交换反应催化性能[J].燃料化学学报, 2016, 44(4):422-427. http://rlhxxb.sxicc.ac.cn/CN/abstract/abstract18809.shtmlFAN Ming-ming, LIU Yan-lei, ZHANG Ping-bo, JIANG Ping-ping.Preparation of magnetic core-shell CaO-MgO@CoFe2O4 solid base and its catalytic performance in the transesterification of soybean oil to biodiesel[J].J Fuel Chem Technol, 2016, 44(4):422-427. http://rlhxxb.sxicc.ac.cn/CN/abstract/abstract18809.shtml