Effects of hydroxyl and hydrogen free radicals on the liquefaction of cellulose in sub/supercritical ethanol
-
摘要: 以水杨酸为羟基自由基(HO·)捕捉剂、四氯化碳为氢自由基(H·)捕捉剂,采用间歇高压反应釜对玉米秸秆纤维素在亚/超临界乙醇中的液化行为进行了研究,通过考察自由基捕捉剂用量、反应温度和反应时间对纤维素液化行为的影响,研究亚/超临界乙醇产生的HO·和H·自由基对纤维素的液化作用。结果表明,随着水杨酸用量增加(0-4 mL),HO·浓度升高,生物油收率由29.3%提高至47.9%,固体残渣收率从26.7%降低至24.3%;反应温度从250 ℃升高至320 ℃,HO·活性随之增强,生物油收率由35.9%升高至58.2%,固体残渣收率由51.8%降低至20.4%;随着四氯化碳用量由0增加为2 mL时,H·浓度降低,生物油收率由24.7%降低至20.7%,固体残渣收率由54.1%增加至59.1%;反应时间从0到30 min,液化作用不断增强,生物油收率从8.7%升高至28.5%,固体残渣收率由86.3%下降至60.9%;30 min之后,四氯化碳对H·活性的抑制加强,导致液化作用减弱,生物油收率有所下降。实验结果表明,乙醇在亚/超临界状态下能够产生HO·和H·,且HO·和H·浓度和活性与反应条件相关,对纤维素液化产物的收率及其分布具有明显的影响。Abstract: With salicylic acid as hydroxyl radical (HO·) trap and carbon tetrachloride as hydrogen radical (H·) trap, the effects of HO· and H· radicals on the liquefaction of cornstalk cellulose in sub/supercritical ethanol was investigated in an autoclave. The results indicated that the concentration of HO· radical increases with the increase of salicylic acid amount added in the feed from 0 to 4 mL; meanwhile, the bio-oil yield is increased from 29.3% to 47.9%, whereas the residue yield is decreased from 26.7% to 24.3%. The activity of HO· increases with the increase of reaction temperature from 250 to 320 ℃; meanwhile, the bio-oil yield is increased from 35.9% to 58.2%, whereas the residue yield is reduced from 51.8% to 20.4%. On the other hand, the concentration of H· radical decreases with the increase of carbon tetrachloride from 0 to 2 mL; meanwhile, the bio-oil yield is decreased from 24.7% to 20.7%, whereas the residue yield is increased from 54.1% to 59.1%. The liquefaction of cellulose is enhanced within 30 min due to the increase of H· activity; after that, the bio-oil yield begins to decline due to the inhibition of H· activity by CCl4. Current results proved that ethanol can produce HO· and H· radicals under sub/supercritical state; the concentration and activity of HO· and H· radicals are dependent on the reaction conditions, which may determine the product yield and distribution for the liquefaction of cellulose in sub/supercritical ethanol.
-
Key words:
- cellulose /
- liquefaction /
- sub/supercritical ethanol /
- free radical /
- radical trap
-
图 3 水杨酸用量对纤维素液化固体残渣的FT-IR谱图
Figure 3 FT-IR spectra of solid residues obtained for cellulose liquefaction with different amounts of salicylic acid in 100mL ethanol under 11-12MPa and 320℃ for 60min
(absorption peak[12-14]: 1060-1160cm-1 C-O; 1710-1770cm-1 -COOH; 1680-1715cm-1 -C=O; 3300-3600cm-1 -O-H)
-
[1] 陈晓菲. 稻秆粉末醇解产物的分析和醇解机理研究[D]. 武汉: 武汉科技大学, 2008.CHEN Xiao-fei. Analysis of the products from alkanolysis of the rice-stalk powder and related mechanism study[D]. Wuhan: Wuhan University of Science and Technology, 2008. [2] HIROIKU K, FUMIO K. Free radical behavior in thermal cracking reaction using petroleum oil and model compounds[J]. Catal Today, 1998, 43: 281-289. doi: 10.1016/S0920-5861(98)00157-6 [3] 黄金保, 刘朝, 魏顺安. 纤维素单体热解机理的热力学研究[J]. 化学学报, 2009, 67(18): 2081-2086. http://www.cnki.com.cn/Article/CJFDTOTAL-HXXB200918006.htmHUANG Jin-bao, LIU Chao, WEI Shun-an. Thermodynamic studies of pyrolysis mechanism of cellulose monomer[J]. Asta Chim Sin, 2009, 67(18): 2081-2086. http://www.cnki.com.cn/Article/CJFDTOTAL-HXXB200918006.htm [4] EDITA J, MATJAZ K, MATIJA S. Cellulose liquefaction in acidified ethylene glycol[J]. Cellulose, 2009, (16): 393-405. https://www.researchgate.net/publication/225106669_Cellulose_liquefaction_in_acidified_ethylene_glycol [5] HESSEIN M, KEAT T L, SUBHASH B, ABDUL R M. Sub/supercritical liquefaction of oil palm fruit press fiber for the production of bio-oil: Effect of solvent [J]. Bioresour Technol, 2010, 101: 7641-7647. doi: 10.1016/j.biortech.2010.04.072 [6] 陶红秀, 解新安, 郑朝阳, 汤成正, 战晓青. 玉米秸秆纤维素在亚/超临界乙醇中的液化行为研究[J]. 西北农林科技大学学报(自然科学版), 2014, (01): 196-204. http://www.cnki.com.cn/Article/CJFDTOTAL-RLHX201301009.htmTAO Hong-xiu, XIE Xin-an, ZHENG Chao-yang, TANG Cheng-zheng, ZHAN Xiao-qing. Liquefaction of cornstalk cellulose in sub/super-critical ethanol[J]. J Northwest A & F Univ (Nat Sci Ed), 2014, (01): 196-204. http://www.cnki.com.cn/Article/CJFDTOTAL-RLHX201301009.htm [7] 姚波, 朱彤, 林伟立. 二羟基苯甲酸的硅烷化及其在气质联用测量气相OH自由基的应用[J]. 环境化学, 2006, 25(6): 773-775. http://www.cnki.com.cn/Article/CJFDTOTAL-HJHX200606026.htmYAO Bo, ZHU Tong, LIN Wei-li. Silanization of DHBAs and measurement of gas phase hydroxyl radicals using Gas Chromatography-Mass Spectrometry[J]. Environ Chem, 2006, 25(6): 773-775. http://www.cnki.com.cn/Article/CJFDTOTAL-HJHX200606026.htm [8] 周建政, 董华进. 用高效液相色谱-电化学检测器法检测Fenton反应中的羟自由基[J]. 中国药理学与毒理学杂志, 1995, 9(4): 299-302. http://www.cnki.com.cn/Article/CJFDTOTAL-YLBS504.017.htmZHOU Jian-zheng, DONG Hua-jin. Determination of hydroxyl radical in fenton reaction by using high performance liquid chromatograph (HPLC) connected with electrochemical detector[J]. Chin J Pharmacol Toxicol, 1995, 9(4): 299-302. http://www.cnki.com.cn/Article/CJFDTOTAL-YLBS504.017.htm [9] RICHMOND R, HALLIWELL B. Formation of hydroxyl radicals from the paraquat radical cation, demonstrated by a highly specific gas chromatographic technique. the role of superoxide radical anion, hydrogen peroxide, and glutathione reductase[J]. J Inorg Biochem, 1982, 17(2): 95-107. doi: 10.1016/S0162-0134(00)80078-1 [10] 聂敏, 王琪, 邱桂花. 氢自由基捕捉剂对苯乙烯超声引发乳液聚合的影响[J]. 高分子学报, 2007, (7): 633-637. http://www.cnki.com.cn/Article/CJFDTOTAL-GFXB200707009.htmNIE Min, WANG Qi, QIU Gui-hua. Effect of Hydrogen radical scavenger on ultrasonically initiated emulsion polymerization of styrene[J]. Acta Polym Sin, 2007, (7): 633-637. http://www.cnki.com.cn/Article/CJFDTOTAL-GFXB200707009.htm [11] 郑朝阳, 解新安, 陶红秀, 郑璐丝, 李雁. 亚/超临界乙醇液化秸秆纤维素解聚反应研究与机理初探[J]. 燃料化学学报, 2012, 40(5): 526-532. http://rlhxxb.sxicc.ac.cn/CN/volumn/volumn_1272.shtml#ZHENG Chao-yang, XIE Xin-an, TAO Hong-xiu, ZHENG Lu-si, LI Yan. Depolymerization of stalk cellulose during its liquefaction in sub-and supercritical ethanol[J]. J Fuel Chem Technol, 2012, 40(5): 526-532. http://rlhxxb.sxicc.ac.cn/CN/volumn/volumn_1272.shtml# [12] SHARYPOV V I, KUZNETSOV B N. Catalytic hydroliquefaction of barzass liptobiolitic coal in a petroleum residue as a solvent[J]. Fuel, 2006, 85(7): 918-922. https://www.researchgate.net/profile/A_Startsev/publication/239142291_Catalytic_hydroliquefaction_of_Barzass_liptobiolitic_coal_in_a_petroleum_residue_as_a_solvent/links/558e189f08ae47a3490bdf8c.pdf?inViewer=true&pdfJsDownload=true&disableCoverPage=true&origin=publication_detail [13] PÜTÜN A E, ÖZCAN A, PÜTÜN E. Pyrolysis of hazelnut shells in a fixed-bed tubular reactor: Yields and structural analysis of bio-oil[J]. J Anal Appl Pyrolysis, 1999, 52(1): 33-49. doi: 10.1016/S0165-2370(99)00044-3 [14] 武景丽, 汪丛伟, 阴秀丽, 吴创之, 马隆龙, 周肇秋, 陈汉平. 基于TG-FTIR的生物油重质组分热解特性研究[J]. 太阳能学报, 2010, 31(1): 113-117. http://www.cnki.com.cn/Article/CJFDTOTAL-TYLX201001023.htmWU Jing-li, WANG Cong-wei, YIN Xiu-li, WU Chuang-zhi, MA Long-long, ZHOU Zhao-qiu, CHEN Han-ping. Study on pyrolysis of heavy fractions of bio-oil by using TG-FTIR analysis[J]. Acta Energ Sol Sin, 2010, 31(1): 113-117. http://www.cnki.com.cn/Article/CJFDTOTAL-TYLX201001023.htm [15] 廖艳芬, 骆仲泱, 王树荣, 余春江, 岑可法. 纤维素快速热裂解机理试验研究Ⅰ.试验研究[J]. 燃料化学学报, 2003, 31(2): 133-138. http://rlhxxb.sxicc.ac.cn/CN/volumn/volumn_1235.shtml#LIAO Yan-fen, LUO Zhong-yang, WANG Shu-rong, YU Chun-jiang, CEN Ke-fa. Mechanism of fast pyrolysis of celluloseⅠ. Experimental research[J]. J Fuel Chem Technol, 2003, 31(2): 133-138. http://rlhxxb.sxicc.ac.cn/CN/volumn/volumn_1235.shtml# [16] 陶红秀, 解新安, 汤成正, 田文广. 玉米秸秆纤维素在亚/超临界乙醇中液化形成酮类化合物的机理探讨[J]. 燃料化学学报, 2013, 41(1): 60-66. http://rlhxxb.sxicc.ac.cn/CN/volumn/volumn_1280.shtml#TAO Hong-xiu, XIE Xin-an, TANG Cheng-zheng, TIAN Wen-guang. Mechanism of ketones formation from cellulose liquefaction in sub-and supercritical ethanol[J]. J Fuel Chem Technol, 2013, 41(1): 60-66. http://rlhxxb.sxicc.ac.cn/CN/volumn/volumn_1280.shtml# [17] 邵千钧, 彭锦星, 修树东, 文先红. 竹子在超临界甲醇中的热解油产物分析[J]. 太阳能学报, 2007, 28(9): 984-987. http://www.cnki.com.cn/Article/CJFDTOTAL-TYLX200709011.htmSHAO Qian-jun, PENG Jin-xing, XIU Shu-dong, WEN Xian-hong. Analysis of oil products by pyrolysis of bamboo in supercritical methanol[J]. Acta Energ Sol Sin, 2007, 28(9): 984-987. http://www.cnki.com.cn/Article/CJFDTOTAL-TYLX200709011.htm [18] SOARES S, RICARDO N M P S, JONES S, HEATLEY F. High temperature thermal degradation of cellulose in air studied using FT-IR and 1H and 13C solid-state NMR[J]. Eur Polym J, 2001, 37(4): 737-745. doi: 10.1016/S0014-3057(00)00181-6 [19] GUO Z, BAI Z, BAI J, WANG Z, LI W. Co-liquefaction of lignite and sawdust under syngas[J]. Fuel Process Technol, 2011, 92(1): 119-125. doi: 10.1016/j.fuproc.2010.09.014