LaFeO3钙钛矿催化湿式氧化苯酚的研究

刘鑫尧 张宣娇 杨淑倩 韩蛟 李印福 张磊 高志贤

刘鑫尧, 张宣娇, 杨淑倩, 韩蛟, 李印福, 张磊, 高志贤. LaFeO3钙钛矿催化湿式氧化苯酚的研究[J]. 燃料化学学报(中英文), 2022, 50(11): 1491-1497. doi: 10.19906/j.cnki.JFCT.2022044
引用本文: 刘鑫尧, 张宣娇, 杨淑倩, 韩蛟, 李印福, 张磊, 高志贤. LaFeO3钙钛矿催化湿式氧化苯酚的研究[J]. 燃料化学学报(中英文), 2022, 50(11): 1491-1497. doi: 10.19906/j.cnki.JFCT.2022044
LIU Xin-yao, ZHANG Xuan-jiao, YANG Shu-qian, HAN Jiao, LI Yin-fu, ZHANG Lei, GAO Zhi-xian. Study on wet air oxidation of phenol catalyzed by LaFeO3 perovskite[J]. Journal of Fuel Chemistry and Technology, 2022, 50(11): 1491-1497. doi: 10.19906/j.cnki.JFCT.2022044
Citation: LIU Xin-yao, ZHANG Xuan-jiao, YANG Shu-qian, HAN Jiao, LI Yin-fu, ZHANG Lei, GAO Zhi-xian. Study on wet air oxidation of phenol catalyzed by LaFeO3 perovskite[J]. Journal of Fuel Chemistry and Technology, 2022, 50(11): 1491-1497. doi: 10.19906/j.cnki.JFCT.2022044

LaFeO3钙钛矿催化湿式氧化苯酚的研究

doi: 10.19906/j.cnki.JFCT.2022044
基金项目: 国家自然科学基金(21673270)和辽宁省教育厅科学研究经费项目(L2019012)资助
详细信息
    通讯作者:

    E-mail: lnpuzhanglei@163.com

    gaozx@lnpu.edu.cn

  • 中图分类号: O643

Study on wet air oxidation of phenol catalyzed by LaFeO3 perovskite

Funds: The project was supported by the National Natural Science Foundation of China (21673270) and the Scientific Research Funds project of Education Department of Liaoning Province (L2019012)
  • 摘要: 本研究采用固相球磨法制备了四种不同球磨时间的LaFeO3钙钛矿催化材料,并将其用于催化湿式氧化苯酚反应,探讨了球磨时间对LaFeO3钙钛矿催化剂催化湿式氧化苯酚水溶液性能的影响。采用XRD、H2-TPR、TG-DTA、FT-IR、N2物理吸附、XPS等手段对LaFeO3钙钛矿催化材料进行了表征。结果表明,在反应温度为200 ℃、空气压力5 MPa、苯酚初始浓度4000 mg/L时,经过240 min的催化氧化反应后LaFeO3-6催化材料最终的COD去除率为94.5%。
  • FIG. 1990.  FIG. 1990.

    FIG. 1990.  FIG. 1990.

    图  1  不同球磨时间LaFeO3的XRD谱图

    Figure  1  XRD patterns of LaFeO3 with different milling time

    a: LaFeO3-4; b: LaFeO3-6; c: LaFeO3-8; d: LaFeO3-10

    图  2  LaFeO3-t的FT-IR谱图

    Figure  2  FT-IR spectra of the LaFeO3-t catalysts

    a: LaFeO3-4; b: LaFeO3-6; c: LaFeO3-8; d: LaFeO3-10

    图  3  LaFeO3-t催化材料的N2吸附-脱附等温线

    Figure  3  N2 adsorption and desorption isotherms of N2 from LaFeO3-t catalytic materials

    a: LaFeO3-4; b: LaFeO3-6; c: LaFeO3-8; d: LaFeO3-10

    图  4  LaFeO3-t催化材料的H2-TPR谱图

    Figure  4  H2-TPR profiles of catalysts LaFeO3-t

    a: LaFeO3-4; b: LaFeO3-6; c: LaFeO3-8; d: LaFeO3-10

    图  5  LaFeO3前驱体的TG-DTA曲线

    Figure  5  TG-DTA curves of LaFeO3 precursor

    图  6  LaFeO3-t催化剂中La 3d的XPS谱图

    Figure  6  XPS spectra of La 3d prepared by LaFeO3-t

    a: LaFeO3-4; b: LaFeO3-6; c: LaFeO3-8; d: LaFeO3-10

    图  7  LaFeO3-t催化剂中Fe 2p的XPS谱图

    Figure  7  XPS spectra of Fe 2p of LaFeO3-t catalyst

    a: LaFeO3-4; b: LaFeO3-6; c: LaFeO3-8; d: LaFeO3-10

    图  8  LaFeO3-t钙钛矿催化剂中O 1s 的XPS 谱图

    Figure  8  XPS spectra of O 1s prepared by LaFeO3-t perovskite catalysts

    a: LaFeO3-4; b: LaFeO3-6; c: LaFeO3-8; d: LaFeO3-10

    图  9  LaFeO3-t钙钛矿复合金属氧化物催化湿式氧化苯酚性能

    Figure  9  CWAO of phenol over the LaFeO3-t catalysts

    表  1  LaFeO3-t的结构参数表

    Table  1  Structural parameters of LaFeO3-t

    CatalystLaFeO3-4LaFeO3-6LaFeO3-8LaFeO3-10
    Specific surface area /(m2·g−1) 15.8 18.2 14.7 14.7
    Pore volume /(cm3·g−1) 0.10 0.08 0.08 0.09
    Average crystallite size /nm 20.7 18.9 20.0 20.9
    下载: 导出CSV

    表  2  LaFeO3-t催化材料的还原峰位置

    Table  2  Reduction of LaFeO3-t catalyst

    CatalystPeak temperature t/℃
    α peakβ peakγ peak
    LaFeO3-4 371 467 673
    LaFeO3-6 333 436 601
    LaFeO3-8 351 448 616
    LaFeO3-10 353 451 636
    下载: 导出CSV

    表  3  LaFeO3-t催化剂中O 1s XPS曲线拟合

    Table  3  O 1s XPS curve-fitting results of LaFeO3-t catalysts

    CatalystOads/(Oads+OLa-O-CO3+Olatt)(%)
    LaFeO3-437.4
    LaFeO3-640.6
    LaFeO3-840.3
    LaFeO3-1039.5
    下载: 导出CSV

    表  4  催化材料的重复使用性

    Table  4  Repetition of the catalyst

    Reuse time1234
    COD removal rate/%94.591.788.285.8
    下载: 导出CSV
  • [1] 蒋博龙, 史顺杰, 蒋海林, 封鑫, 孙好芬. 金属有机框架材料吸附处理苯酚污水机理研究进展[J]. 化工进展,2021,40(8):4525−4539.

    JIANG Bo-long, SHI Shun-jie, JIANG Hai-lin, FENG Xin, SUN Hao-fen. Research progress in phenol adsorption mechanism over metal-organic framework from wastewater[J]. Chem Ind Eng Prog,2021,40(8):4525−4539.
    [2] 于喜洋, 顾贵洲, 李政. 水滑石材料处理工业废水的研究进展[J]. 石油化工高等学校学报,2021,34(6):16−21. doi: 10.3969/j.issn.1006-396X.2021.06.003

    YU Xi-yang, GU Gui-zhou, LI Zheng. Research progress of industrial wastewater treatment by hydrotalcite[J]. J Petrochem Univ,2021,34(6):16−21. doi: 10.3969/j.issn.1006-396X.2021.06.003
    [3] MA C J, WEN Y Y, YUE Q Q, LI A Q, FU J L, ZHANG N W, GAI H J, ZHENG J B, CHEN B H. Oxygen-vacancy-promoted catalytic wet air oxidation of phenol from MnO2-CeO2[J]. RSC Adv,2017,7(43):27079−27088. doi: 10.1039/C7RA04037G
    [4] 王建兵, 祝万鹏, 王伟, 杨少霞. 颗粒Ru催化剂催化湿式氧化乙酸和苯酚[J]. 中国环境科学,2007,27(2):179−183.

    WANG Jian-jun, ZHU Wan-peng, WANG Wei, YANG Shao-xia. Catalytic wet air oxidation of acetic acid and phenol with pelletized ruthenium catalyst Ru/ZrO2-CeO2 catalysts[J]. Chin Environ Sci,2007,27(2):179−183.
    [5] PLEŞA C R, COTEŢ L C, MĂICĂNEANU A, VASILESCU M, VULPOI A. Preparation, characterization, and testing of metal-doped carbon xerogels as catalyst for phenol CWAO[J]. Environ Sci Pollut Res,2016,24(3):2980−2986.
    [6] 张宣娇, 孙羽, 刘明, 郝书敏, 杨涛, 张磊, 白金, 韩蛟. CeO2形貌结构对催化湿式空气氧化苯酚性能的影响[J]. 中国环境科学,2020,40(10):4330−4334. doi: 10.3969/j.issn.1000-6923.2020.10.016

    ZHANG Xuan-jiao, SUN Yu, LIU Ming, HAO Shu-min, YANG Tao, ZHANG Lei, BAI Jin, HAN Jiao. Effect of morphology on the performance of CeO2 for catalytic wet air oxidation of phenol[J]. Chin Environ Sci,2020,40(10):4330−4334. doi: 10.3969/j.issn.1000-6923.2020.10.016
    [7] WANG D Z, LUO X Y, YANG S P, XUE G. Tourmaline/Perovskite composite material as heterogeneous catalysts for activation peroxymonosulfate to remove organic dye in water[J]. J Environ Chem Eng,2021,9(54):105221.
    [8] JIMÉNEZ R, ZAMORE R, PECCHI G, GARCIAGARCIA X, GORDON A L. Effect of Ca-substitution in La1−xCaxFeO3 perovskites on the catalytic activity for soot combustion[J]. Fuel Process Technol,2010,91(5):546−549. doi: 10.1016/j.fuproc.2009.12.017
    [9] VIJAYARAGHAVAN T, ALTHAF R, BABU P, PARIDA K M, VADIVEL S, ASHOK A M. Visible light active LaFeO3 nano perovskite-RGO-NiO composite for efficient H2 evolution by photocatalytic water splitting and textile dye degradation[J]. J Environ Chem Eng,2021,9(1):104675. doi: 10.1016/j.jece.2020.104675
    [10] WU S H, LIN Y, YANG S P, DU C, TENG Q, MA Y, ZHANG D M, NIE L J, ZHONG Y Y. Enhanced activation of peroxymonosulfte by LaFeO3 perovskite supported on Al2O3 for degradation of organic pollutants[J]. Chemosphere,2019,237:124478. doi: 10.1016/j.chemosphere.2019.124478
    [11] SUN W J, LV H X, MA L, TAN X D, JIN C Y, WU H L, CHEN L L, LIU M Y, WEI H Z, SUN C L. Use of catalytic wet air oxidation (CWAO) for pretreatment of high-salinity high-organic wastewater[J]. J Environ Sci,2022,120:105−114. doi: 10.1016/j.jes.2021.06.027
    [12] 白金, 丁力, 刘鑫尧, 王新明, 张磊, 韩蛟, 刘道胜, 王香攀. 原位合成CuO/ZnO-Al2O3水滑石衍生催化剂催化湿式空气氧化苯酚[J]. 环境科学学报,2018,38(6):2360−2366.

    BAI Jin, DING Li, LIU Xin-yao, WANG Xin-ming, ZHANG Lei, HAN Jiao, LIU Dao-sheng, WANG Xiang-pan. In-situ systhesis of CuO /ZnO-Al2O3 catalysts derived from hydrotalcite precursor for catalytic wet air oxidation of phenolic[J]. Acta Sci Circum,2018,38(6):2360−2366.
    [13] 邓禺南, 陈炜鸣, 罗梓尹, 崔瑜旗, 李启彬. MnO2催化O3处理准好氧矿化垃圾床渗滤液尾水中难降解有机物[J]. 中国环境科学,2018,38(11):132−142.

    DENG Yu-nan, CHEN Wei-ming, LUO Zi-yin, CUI Yu-qi, LI Qi-bin. Removal of refractory organics from SAARB treated landfill leachate by O3/MnO2 process[J]. Chin Environ Sci,2018,38(11):132−142.
    [14] 傅潇然. 一种新型在线紫外水质分析仪的研制[D]. 天津: 天津大学, 2008.

    FU Xiao-Ran. Development of a new kind of on-line ultraviolet spectroscopic water quality analyaer[D]. Tianjin: Tianjin University, 2008.
    [15] SENNA M, BILLIK P, YERMAKOV A Y, ŠKRÁTEK M, MAJEROVÁ M, ČAPLOVIčOVÁ M, NOSKO M. Synthesis and magnetic properties of CuAlO2 from high-energy ball-milled Cu2O-Al2O3 mixture[J]. J Alloy Compd,2017,695:2314−2323. doi: 10.1016/j.jallcom.2016.11.097
    [16] CHAUDHARI V, SHIRSATH S E, MANE M L, KADAM R H, SHELKE S B, MANE D R. Crystallographic, magnetic and electrical properties of Ni0.5Cu0.25Zn0.25LaxFe2−xO4 nanoparticles fabricated by sol-gel method[J]. J Alloy Compd,2013,549:213−220. doi: 10.1016/j.jallcom.2012.09.060
    [17] 徐俊峰, 刘坚, 赵震, 张桂臻, 段爱军, 姜桂元, 徐春明. 三维有序大孔钙钛矿LaFeO3催化剂的制备及其催化炭黑颗粒燃烧性能[J]. 催化学报,2010,31(2):236−241.

    XU Jun-feng, LIU Jian, ZHAO Zhen, ZHANG Gui-zhen, DUAN Ai-jun, JIANG Gui-yuan, XU Chun-ming. Preparation and catalytic performance of three-dimensionally ordered macroporous perovskite-type LaFeO3 catalyst for soot combustion[J]. Chin J Catal,2010,31(2):236−241.
    [18] 胡瑞生, 谭立志, 王欣, 孙艳, 胡佳楠, 赵文岩. 掺杂型稀土双钙钛矿光催化剂La2FeTiO6葡萄糖络合法制备与表征[J]. 中国稀土学报,2012,30(5):550−555.

    HU Rui-sheng, TAN Li-zhi, WANG Xin, SUN Yan, HU Jia-nan, ZHAO Wen-yan. Preparation and characterization of doped rare earth double perovskite-type photocatalyst La2FeTiO6 by glucose complex method[J]. J Chin Rare Earth Soc,2012,30(5):550−555.
    [19] LEVASSEUR B, KALIAGUINE S. Methanol oxidation on LaBO3 (B=Co, Mn, Fe) perovskite-type catalysts prepared by reactive grinding[J]. Appl Catal A: Gen,2008,343(1/2):29−38. doi: 10.1016/j.apcata.2008.03.016
    [20] 杨彩虹, 韩怡卓, 李文彬. Ni-La2O3/C催化剂上甲醇羰基化反应性能的研究[J]. 燃料化学学报,2000,28(5):392−395. doi: 10.3969/j.issn.0253-2409.2000.05.003

    YANG Cai-hong, HAN Yi-zhuo, LI Wen-bin. Effect of La2O3 on Ni/C catalysts for vapor phase carbonylation of methanol[J]. J Fuel Chem Technol,2000,28(5):392−395. doi: 10.3969/j.issn.0253-2409.2000.05.003
    [21] MICKEVIČIUS S, GREBINSKIJ S, BONDARENKA V, VENGALIS B, ŠLIUŽIENĖ K, ORLOWSKI B A, DRUBE W. Investigation of epitaxial LaNiO3−x thin films by high-energy XPS[J]. J Alloy Compd,2006,423(1):107−111.
    [22] HONMA T, BENINO Y, FUJIWARA T, KOMATSU T, SATO R, DIMITROV V. Electronic polarizability, optical basicity, and interaction parameter of La2O3 and related glasses[J]. J Appl Phys,2002,91(5):2942−2950. doi: 10.1063/1.1436292
    [23] WU M D, MA S W, CHEN S Y, XIANG W G. Fe–O terminated LaFeO3 perovskite oxide surface for low temperature toluene oxidation[J]. J Clean Prod,2020,277:123224. doi: 10.1016/j.jclepro.2020.123224
    [24] WANG H H, GUO Z Q, HAO W T, ZHANG Y J, CAO E S. Ethanol sensing characteristics of BaTiO3/LaFeO3 nanocomposite[J]. Mater Lett,2018,234:40−44.
    [25] CAO E S, QIN Y R, CUI T T, SUN L, HAO W T, ZHANG Y J. Influence of Na doping on the magnetic properties of LaFeO3 powders and dielectric properties of LaFeO3 ceramics prepared by citric sol-gel method[J]. Ceram Int,2017,43(10):7922−7928. doi: 10.1016/j.ceramint.2017.03.119
  • 加载中
图(10) / 表(4)
计量
  • 文章访问数:  340
  • HTML全文浏览量:  122
  • PDF下载量:  46
  • 被引次数: 0
出版历程
  • 收稿日期:  2022-03-21
  • 修回日期:  2022-05-02
  • 录用日期:  2022-05-05
  • 网络出版日期:  2022-06-09
  • 刊出日期:  2022-11-30

目录

    /

    返回文章
    返回